After cold rolling of AA 8091 alloy by 5%∼30%, the static recrystallization kinetics were studied in the range of temperature from 350℃ to 500℃ with varying isothermal holding time from 1 to 5000 sec. It was observed that all recrystallized grai...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A3232931
1992
Korean
436
KCI등재
학술저널
59-67(9쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
After cold rolling of AA 8091 alloy by 5%∼30%, the static recrystallization kinetics were studied in the range of temperature from 350℃ to 500℃ with varying isothermal holding time from 1 to 5000 sec. It was observed that all recrystallized grai...
After cold rolling of AA 8091 alloy by 5%∼30%, the static recrystallization kinetics were studied in the range of temperature from 350℃ to 500℃ with varying isothermal holding time from 1 to 5000 sec. It was observed that all recrystallized grains were nucleated at the grain boundaries which were formed during cold rolling and grown. The kinetics of recrystallization could be well described by Avrami equation, Y=1-exp(-ktⁿ) and the values of n were found to be in the range from 0.35 to 0.48 and those of k were known to be in the range from 8 × 10^(-2) to 3 × 10^(-1). It was found that the values of n were lower than those of any other Al alloys which have the value of 0.6, and therefore the recrystallization of AA 8091 alloy could be restricted by the precipitates of δ' and Al₃Zr. It was observed that the fast recrystallization rate was assisted by dislocation elimination, precitates coarsening and large amount of δ' resolution in Al matrix at higher temperatures than 450℃ and the effect of temperature on the recrystallization rate was more pronounced than that of prestrain on the rate at higher prestrains than 10 percents.
Cu-Ni 고용체 합금의 정적 및 반복응력 Creep 변형에 미치는 용질원자의 영향
국내산 황산니켈로부터 수소환원법에 의한 고순도 Ni 분말의 제조