<P>The micro-hardness and electric conductivity was studied in as cast alloy Cu-Fe-P alloys which were solution treated at 980°C and aging treated at 400-800°C for 1-20 hours. The micro-hardness peak value was 180 HV and the conductivity...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107602423
2009
-
SCOPUS
학술저널
267-270(4쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P>The micro-hardness and electric conductivity was studied in as cast alloy Cu-Fe-P alloys which were solution treated at 980°C and aging treated at 400-800°C for 1-20 hours. The micro-hardness peak value was 180 HV and the conductivity...
<P>The micro-hardness and electric conductivity was studied in as cast alloy Cu-Fe-P alloys which were solution treated at 980°C and aging treated at 400-800°C for 1-20 hours. The micro-hardness peak value was 180 HV and the conductivity peak value was 65% IACS. The hardness and the electric conductivity all depended on precipitation principally. The addition of C in Cu-Fe-P alloy reduced the grain size and accelerated precipitation which resulted in enhancing hardness and electric conductivity together.</P>
Effects of Flow Characteristics in Polymer Electrolyte Membrane Fuel Cell
Synthesis of Zeolite Added Clay and Sewage Sludge