초음파 분무 열분해법으로 제조한 텅스텐 분말의 상압소결과 미세조직 = Pressureless Sintering and Microstructure of Pure Tungsten Powders Prepared by Ultrasonic Spray Pyrolysis

다국어 초록 (Multilingual Abstract)

This study demonstrates the effect of the compaction pressure on the microstructure and properties of pressureless-sintered W bodies. W powders are synthesized by ultrasonic spray pyrolysis and hydrogen reduction using ammonium metatungstate hydrate as a precursor. Microstructural investigation reveals that a spherical powder in the form of agglomerated nanosized W particles is successfully synthesized. The W powder synthesized by ultrasonic spray pyrolysis exhibits a relative density of approximately 94% regardless of the compaction pressure, whereas the commercial powder exhibits a relative density of 64% under the same sintering conditions. This change in the relative density of the sintered compact can be explained by the difference in the sizes of the raw powder and the densities of the compacted green body. The grain size increases as the compaction pressure increases, and the sintered compact uniaxially pressed to 50 MPa and then isostatically pressed to 300 MPa exhibits a size of 0.71 m. The Vickers hardness of the sintered W exhibits a high value of 4.7 GPa, mainly due to grain refinement.

참고문헌 (Reference)

1 Y.-N. Liu, 455 : 676-, 2014

2 Z. Z. Fang, 53 : 326-, 2008

3 L. J. Kecskes, 26 : 2407-, 1995

4 Z. Zhou, 505 : 131-, 2009

5 M. A. Monge, 386-388 : 613-, 2009

6 J. M. Byun, 99 : 105602-, 2021

7 I. H. Moon, 102 : 219-, 1984

8 R. M. German, 23 : 77-, 2005

9 P. Garg, 25 : 16-, 2007

10 R. Malewar, 22 : 1200-, 2007

11 K. Heinola, 107 : 113531-, 2010

12 R. M. German, 49 : 19-, 2006

13 Y. Wang, 40 : 171-, 2021

14 A. S. Abdallah, 1 : 17-146, 2017

15 조현희 ; 김정현 ; 이영인 ; 정영근 ; 오승탁, "초음파 분무 열분해법으로 제조한 텅스텐 미세분말의 미세조직과 소결 거동" 대한금속·재료학회 59 (59): 289-294, 2021

16 권나연 ; 정영근 ; 오승탁, "나노-마이크로 크기 하이브리드 구조 텅스텐 분말특성에 미치는 분말혼합 공정의 영향" 한국분말재료학회 24 (24): 384-388, 2017

17 문환균 ; 홍경태 ; 김선진, "기계적 합금화환( Al+12.5%Cu)3Zr 초미립 금속간화합물의 CIP 성형 및 소결 거동" 한국재료학회 12 (12): 634-640, 2002