배선 함몰 전극의 배선 소결공정 최적화에 따른 전기적 특성 향상

다국어 초록 (Multilingual Abstract)

To substitute indium tin oxide (ITO), many substituents have been studied such as metal nanowires, carbon based materials, 2D materials, and conducting polymers. These materials are not good enough to apply to an electrode because theses exhibit relatively high resistance. So metal grids are required as an additionalelectrode to improve the conductivities of substituents. The metal grids were printed by electrohydrodynamic printing system using Ag nanoparticle based ink. The Ag grids showed high uniformity and the line width was about 10 μm. The Ag nanoparticles are surrounded by dispersants such as unimolecular and polymer to prevent aggregation between Ag nanoparticles. The dispersants lead to low conductivity of Ag grids. Thus, the sintering process of Ag nanoparticles is strongly recommended to remove dispersants and connect each nanoparticles. For sintering process, the interface and microstructure of the Ag grid were controlled in 1.0 torr Ar atmosphere at aound 400oC of temperature. From the sintering process, the uniformity of the Ag grid was improved and the defects on the Ag grids were reduced. As a result, the resistivity of Ag grid was greatly reduced up to 5.03(±0.10) × 10<SUP>-6</SUP> Ω·cm. The metal grids embedded substrates containing low pressure Ar sintered Ag grids showed 90.4% of transmittance in visible range with 0.43 Ω/□ of sheet resistance.

목차 (Table of Contents)

• Abstract
• 1. 서론
• 2. 실험방법
• 3. 결과 및 고찰
• 4. 결론
• References

참고문헌 (Reference)

1 Han-Ki Kim, 28 : 1-, 2010

2 S. Jung, 4 : 1300474-, 2014

3 Y. H. Kim, 21 : 1076-, 2011

4 J. S. Yu, 4 : 6032-, 2012

5 Y. Galagan, 104 : 32-, 2012

6 Y. Galagan, 95 : 1339-, 2011

7 J. R. Greer, 55 : 6345-, 2007

8 K. Park, 313 : 351-, 2008

9 H. S. Kim, 97 : 791-, 2009

10 S. Hong, 7 : 5024-, 2013

11 J. Yeo, 246 : 562-, 2014

12 J. Perelaer, 18 : 2101-, 2006

13 J. Perelaer, 21 : 4830-, 2009

14 M. L. Allen, 19 : 175201-, 2008

15 D. Wakuda, 441 : 305-, 2007

16 D. Wakuda, 59 : 649-, 2008

17 S. Magdassi, 4 (4): 1943-, 2010

18 M. Grouchko, 5 (5): 3354-, 2011

19 S. I. Na, 20 : 4061-, 2008