WC-10Co4Cr으로 초고속 화염용사 코팅된 Cu 합금의 해수내 캐비테이션 손상 거동

다국어 초록 (Multilingual Abstract)

Due to the good corrosion resistance and machinability, copper alloy is commonly employed for shipbuilding, hydroelectric power and tidal power industries. The Cu alloy, however, has poor durability, and the seawater application at fast flow condition becomes vulnerable to cavitation damage leading to economic loss and risking safety. The HVOF(High Velocity Oxygen Fuel) thermal spray coating with WC-10Co4Cr were therefore introduced as a replacement for chromium or ceramic to minimize the cavitation damage and secure durablility under high-velocity and high-pressure fluid flow. Cavitation test was conducted in seawater at 15℃ and 25℃ with an amplitude of 30 μm on HVOF WC-10Co4Cr coatings produced by thermal spray. The cavitation at 15℃ and 25℃ exposed the substrate in 12.5 hours and in 10 hours, respectively. Starting from 5 hours of cavitation, the coating layer continued to show damage by higher than 160% over time when the temperature of seawater was elevated from 15℃ to 25℃. Under cavitation environment, although WC-10Co4Cr has good wear resistance and durability, increase in temperature may accelerate the damage rate of the coating layer mainly due to cavitation damage.

목차 (Table of Contents)

• Abstract
• 1. 서론
• 2. 실험 방법
• 3. 실험내용 및 고찰
• 4. 결론
• 참고문헌

참고문헌 (Reference)

1 J. T. Chang, 255 : 162-169, 2003

2 A. A. Bouudi, 173 : 44-52, 2006

3 T. Y. Cho, 26 : 1325-, 2007

4 J. E. Cho, 200 : 2653-2662, 2006

5 P. Chivavibul, 202 : 509-521, 2007

6 Y.-Q. Zhang, 39 (39): 25-29, 2010

7 S. Mattnew, 51 : 1172-1180, 2009

8 A. G. Petersen, 60 : 187-194, 2004

9 송기오, "최적 고속화염용사법으로 제조된 WC-CoCr 코팅층의 마모 특성" 대한금속·재료학회 46 (46): 351-356, 2008

10 김길수, "초고속 스핀들의 내구성 향상을 위한 WC-Co 분말의 HVOF 용사 코팅" 한국표면공학회 39 (39): 179-189, 2006

11 조재억, "산성용액에서의 WC계 초경 용사코팅층의 부식거동" 대한금속·재료학회 42 (42): 1005-1013, 2004

12 권기봉, "HVOF를 이용한 Fe-Cr-Ni-Mo-Si-B계 고성능 합금 용사층의 특성에 미치는 용사조건의 영향" 한국표면공학회 35 (35): 5-10, 2002

13 어광준, "HVOF 용사에 의한 WC-CoCr 코팅 최적화를 위한 다구치 실험계획방법의 적용" 대한금속·재료학회 45 (45): 292-299, 2007

14 조동율, "Comparison of HVOF Thermal Spray Coatings of T800 and WC-Co Powders" 한국표면공학회 39 (39): 295-301, 2006

15 "Annual Book of ASTM Standards G32-92"