$Co_xMn_{3-x}O_4$ ($1.48{\leq}x{\leq}1.63$) ceramics were fabricated using the solid-state reaction method. Structural and electrical properties of specimens based on the composition ratio of Co were observed in order to investigate their applicabilit...
$Co_xMn_{3-x}O_4$ ($1.48{\leq}x{\leq}1.63$) ceramics were fabricated using the solid-state reaction method. Structural and electrical properties of specimens based on the composition ratio of Co were observed in order to investigate their applicability in NTC thermistors. All specimens showed a single spinel phase with a homogeneous tetragonal structure. The $Co_{1.57}Mn_{1.43}O_4$ specimen showed a maximum average grain size of approximately $6.47{\mu}m$. In all specimens, TCR properties displayed excellent characteristics of over $-4.2%/^{\circ}C$. The resistivity at 298 K and B-value of the $Co_{1.57}Mn_{1.43}O_4$ specimen were approximately $418{\Omega}-cm$ and 4300, respectively.