STS 440C 마르텐사이트계 스테인리스 강의 열처리에 따른 미세조직, 기계적 특성 및 부식 거동

다국어 초록 (Multilingual Abstract)

Martensitic stainless steel is commonly used in the medical implant instrument. The alloy has drawbacks in terms of strength and wear properties when applied to instruments with sharp parts. 440C STS alloy, with improved durability, is an alternative to replace 420 J2 STS. In the present study, the carbide precipitation, and mechanical and corrosion properties of STS 440C alloy are studied as a function of different heat treatments. The STS 440C alloy is first austenitized at different temperatures; this is immediately followed by oil quenching and sub-zero treatment. After sub-zero treatment, the alloy is tempered at low temperatures. The microstructures of the heat treated STS 440C alloy consist of martensite and retained austenite and carbides. Using EDX and SADP with a TEM, the precipitated carbides are identified as a Cr23C6 carbide with a size of 1 to 2 μm. The hardness of STS 440C alloy is improved by austenitization at 1,100 oC with sub-zero treatment and tempering at 200 oC. The values of Ecorr and Icorr for STS 440C increase with austenitization temperature. Results can be explained by the dissolution of Cr-carbide and the increase in the retained austenite. Sub-zero treatment followed by tempering shows a little difference in the properties of potentiodynamic polarizations.

목차 (Table of Contents)

• Abstract
• 1. 서 론
• 2. 실험방법
• 2.1 STS 440C 시편
• 2.2 STS 440C의 열처리 공정
• 2.3 미세조직 및 결정구조 분석
• 2.4 경도 측정
• 2.5 동전위 분극 시험
• 3. 결과 및 고찰
• 3.1 미세 조직 특성
• 3.2 기계적 특성
• 3.3 부식 거동
• 4. 결 론
• References

참고문헌 (Reference)

1 A. N. Isfahany, 509 : 3931-, 2011

2 J. Y. Park, 62 : 541-, 2006

3 H. H. Lu, 240 : 275-, 2019

4 A. N. Isfahany, 509 : 3931-, 2011

5 M. Albertini, 79 : 163-, 2012

6 C. J. Scheuer, 317 : 70-, 2019

7 A. A. Salih, 5 : 867-, 2011

8 J. R. Yang, 438-440 : 276-, 2006

9 C. T. Kwok, 166 : 221-, 2003

10 S. H. Salleh, 4 : 123-, 2009

11 M. A. Neri, 47 : 283-, 2001

12 C. G. De Andres, 241 : 211-, 1998

13 Z. X. Xia, 528 : 6764-, 2011

14 S. Y. Lu, 165 : 45-, 2015

15 A. F. Candelaria, 22 : 1151-, 2003

16 A. Rajasekhar, 30 : 1612-, 2009

17 L. Ning, 7 : 1057-, 1991

18 J. Y. Park, 448–451 : 1131-, 2007

19 T. Tsuchiyama, 532 : 585-, 2012