Burn Damage에 따른 도막의 방청성 평가 = Evaluation of the Corrosion Protection Coating in Accordance with Burn Damage

다국어 초록 (Multilingual Abstract)

This study was conducted in order to examine the effect of burn damage and the resultant anti-corrosion performance. The breakdown and defect of the paint film caused by burn damage are considered to affect not only the macroscopic appearance but also the adhesive force and the anti-corrosion performance of the paint film. The material of the paint film was epoxy paint that is used most widely for heavy-duty coating, and in order to induce burn damage, heat treatment with a torch was applied to the other side of the paint film. Surface and chemical structure changes according to aging were analyzed using FE-SEM and infrared absorption spectroscopy, and variation in the anti-corrosion performance was analyzed through the AC impedance test.

참고문헌 (Reference)

1 Z. Paley, 24 : 83-, 1994

2 C. K. Park, 41 : 103-, 2013

3 A. Amirudin, 26 : 1-, 1995

4 M. Hulden, 13 : 171-, 1985

5 O. Knudsen, 54 : 224-, 2005

6 M. Hulden, 13 : 171-, 1985

7 H. Leidheiser, 70 : 121-, 1987

8 A. Kalendova, 46 : 324-, 2003

9 H. Leidheiser, "Polymeric Materials for Corrosion Control, ACS Symp. Ser" 124-, 1986

10 C. H. Hare, "Paint Film Degradation Mechanisms and Controls" SSPC 205-, 2001

11 B. Stratman, "Encyclopedia of Electrochemistry Corrosion and Oxide Films" 460-, 2001