고속열간압연가공된 AA1050의 두께방향으로의 변형량 및 미세조직 변화 = Through-Thickness Variation of Strain and Microstructure of AA1050 Processed by High Speed Hot Rolling

다국어 초록 (Multilingual Abstract)

The through-thickness variations of strain and microstructure of high-speed hot rolled 1050 pure aluminum sheet were investigated. The specimens of 1050 aluminum were rolled at temperatures ranging from 410 to $560^{\circ}C$ at a rolling speed of 15 m/s without lubrication and quenched in water at an interval of 30ms after rolling. The redundant shear strain induced by high friction between rolls and the aluminum sheet was increased largely beneath the surface at a rolling reduction above 50%. Recrystallization occurred in the surface regions of the specimen rolled to reduction of 65% at $510^{\circ}C$, while only recovery occurred in the other regions.

참고문헌 (Reference)

1 W. C. Liu, 472 : 170-, 2008

2 S. B. Kang, 10 : 761-, 1997

3 H. S. Ko, 35 : 1699-, 1997

4 J. K. Lee, 50 : 869-, 2007

5 H. Utsunomiya, 57 : 1109-, 2007

6 I. L. Dilamore, 12 : 281-, 1964

7 M.F. Ashby, 21 : 399-, 1970

8 T. Sakai, 1998

9 W. Truskowski, 11 : 749-, 1980

10 T. Sakai, 27 : 520-, 1987

11 T. Sakai, 31 : 86-, 1991

12 T. Sakai, 28 : 1029-, 1987

13 Seong-Hee Lee, "Microstructure and Texture Development of Pure Aluminum and Aluminum Alloy Processed by High Speed Hot Rolling" 대한금속·재료학회 14 (14): 263-268, 2008