슈퍼듀플렉스강 용접금속의 입계부식에 미치는 σ상의 영향 = Research Effect of σ-phase on Intergranular Corrosion of Super Duplex Stainless Steel Weld Metal

다국어 초록 (Multilingual Abstract)

A specimen of weld metal was prepared by GTA welding with weld wire of super duplex stainless steel. Aging treatment was conducted for the sample at the temperature range of 700 to 900℃ for 5 to 300 minutes. The effect of volume fraction of σ-phase to intergranular corrosion of weld metal has been investigated and the results were derived as follows. The volume fraction of σ phase tends to increase with an increase of aging temperature and time and intergranular corrosion of weld metal was increased by an increase of σ phase. Degree of sensitization representing intergranular corrosion was found to tend to increase with an increase of aging time at 700 to 800℃, while it decreased by an increase of aging time at 900℃.

참고문헌 (Reference)

1 Nathalie Lopez, 229 : 123-128, 1997

2 K. Ravindranath, 37 : 121-132, 1995

3 C. J. Park, 61 : 76-83, 2005

4 N. Ebrahimi, 53 : 637-644, 2011

5 Mehmet Emin ARIKAN, 32 : 323-335, 2008

6 SC. Duret-Thual, 52 : 37-44, 2001

7 Franc Tehovnik, 45 : 339-345, 2011

8 Ciofu Florin, Welding in theDuplex Stainless Steel 52-59, 2010

9 B. Gideon, 7 : 247-263, 2008

10 N. Lopez, 41 : 1615-1631, 1999

11 T. Ogawa, 68 : 181-191, 1989

12 J. H. Potgieter, 50 : 2572-2579, 2008

13 L. Karlsson, 43 : 20-41, 1999