Inconel 617의 고온열화에 따른 미세구조 및 고온 기계적 특성 = Effect of High Temperature Degradation on Microstructure and High Temperature Mechanical Properties of Inconel 617

다국어 초록 (Multilingual Abstract)

Inconel 617 is a candidate tube material for high temperature gas-cooled reactors(HTGR). The microstructure and mechanical properties of Inconel 617 were studied after exposure at high temperature($1050^{\circ}C$). The dominant oxide layer was Cr-oxide. The internal oxide and Cr-depleted region were observed below the Cr-oxide layer. The depth of Cr-depleted zone and internal oxide increased with exposure time. The major phases of carbides are $M_{23}C_6\;and\;M_6C$. The composition of $M_{23}C_6\;and\;M_6C$ were determined to be Cr-rich and Mo-rich, respectively. $M_6C$ carbide is more stable than $M_{23}C_6$ at high temperature. From the results of high temperature compression test, there were no significant changes in hardness and yield strength upon increasing exposure time.

참고문헌 (Reference)

1 Kihara Shigemitu, "제목없음" 11 : 1019-, 1980

2 W. L. Mankins, "제목없음" 5 : 1579-, 1974

3 N. S. Cheruvu, "제목없음" 20 : 87-, 1989

4 Z. Qu, "제목없음" 12 : 1333-, 1981

5 F. Schubert, "제목없음" 66 : 227-, 1984

6 M. Yamashita, "제목없음" 37 : 1133-, 1997

7 Tsutomu Takahashi, "제목없음" 18 : 221-, 1978

8 Moon DP, "제목없음" 5 : 754-, 1998

9 Esmaeili S, "제목없음" 32 : 1777-, 1995

10 Toshiyuki Hirano, "제목없음" 12 : 451-, 1981

11 C. T. Sims, "제목없음" 257 : 1987-,

12 J.C.Kim, "제목없음" 26 : 245-, 1997

13 H.M. Yun, "제목없음" 125 : 258-, 1984

14 Tawancy HM, "제목없음" 29 : 689-, 1993