Self-Separation 방법을 적용한 고품질 Free-Standing GaN
손호기,이영진,김진호,황종희,전대우,이혜용,Son, Ho Ki,Lee, Young Jin,Kim, Jin-Ho,Hwang, Jonghee,Jeon, Dae-Woo,Lee, Hae-Yong 한국전기전자재료학회 2016 전기전자재료학회논문지 Vol.29 No.11
We demonstrated that self-separation FS-GaN (freestanding-GaN) was grown on MELO (maskless epitaxially lateral overgrowth) GaN template by horizontal HVPE (hydride vapor phase epitaxy). Before thick GaN grwoth, MELO GaN template was grown on patterned GaN template by MOCVD (metal organic chemical vapor deposition). The laterally overgrown GaN would consist of a continuous well coalesced layer. The mixed TDD (threading dislocation density) of seed and wing region were $8{\times}10^8cm^{-2}$ and $7{\times}10^7cm^{-2}$, respectively. After thick GaN grown by HVPE, the self-separation between thick GaN and sapphire substrate was generated at seed region. The regions of self-separation for FS-GaN and sapphire were observed by FE-SEM. Moreover, Raman results indicated that the compressive strain of seed and wing regions at FS-GaN substrate were slightly released compared to that of thick GaN grown on conventional GaN template. The optical properties of the FS-GaN substrate were examined by using PL (photoluminescence). The PL exhibited that donor bound exciton and donor acceptor pair were observed at low temperature. The effects on optical and structural properties of FS-GaN substrate have been discussed in detail.
FS-GaN을 열산화하여 제작된 Beta-Ga<sub>2</sub>O<sub>3</sub> 박막의 특성
손호기,이영진,이미재,김진호,전대우,황종희,이혜용,Son, Hoki,Lee, YoungJin,Lee, Mijai,Kim, Jin-Ho,Jeon, Dae-Woo,Hwang, Jonghee,Lee, Hae-Yong 한국전기전자재료학회 2017 전기전자재료학회논문지 Vol.30 No.7
In this paper, we discuss ${\beta}-Ga_2O_3$ thin films that have been grown on freestanding GaN (FS-GaN) using furnace oxidation. A GaN template was grown by horizontalhydride vapor phase epitaxy (HVPE), and FS-GaN was fabricated using the laser lift off (LLO) system. To obtain ${\beta}-Ga_2O_3$ thin film, FS-GaN was oxidized at $900{\sim}1,100^{\circ}C$. Surface and cross-section of prepared ${\beta}-Ga_2O_3$ thin films were observed by field emission scanning electron microscopy (FE-SEM). The single crystal FS-GaNs were changed to poly-crystal ${\beta}-Ga_2O_3$. The oxidized ${\beta}-Ga_2O_3$ thin film at $1,100^{\circ}C$ was peel off from FS-GaN. Next, oxidation of FS-GaNwas investigated for 0.5~12 hours with variation of the oxidation time. The thicknesses of ${\beta}-Ga_2O_3$ thin films were measured from 100 nm to 1,200 nm. Moreover, the 2-theta XRD result indicated that (-201), (-402), and (-603) peaks were confirmed. The intensity of peaks was increased with increased oxidation time. The ${\beta}-Ga_2O_3$ thin film was generated to oxidize FS-GaN.