Saamia Zahid,Muhammad Ali Nasir,Saad Nauman,Mehmet Karahan,Yasir Nawab,H. M. Ali,Yasir Khalid,Muhammad Nabeel,Mudaser Ullah 대한기계학회 2019 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.33 No.1
In this study experimental investigation of interlaminar shear strength of glass fibre reinforced thermoplastic polyurethane (TPU) and epoxy based thermosets composites enhanced with multi walled carbon nanotubes (MWCNTs) is presented, and comparison is made between thermoplastic and thermosets composites. Suspension of MWCNTs in TPU and epoxy matrix was prepared using magnetic stirring and sonication technique. Both thermoplastic reinforced glass fibre and thermosets reinforced glass fibre composites were manufactured using hand layup technique. Carbon nanotubes were added in the concentrations of 0.1 %weight, 0.3 %weight and 0.5 %weight in both types of composites. Results showed that as the concentration of CNTs increases, the ILSS of the nanocomposites was also improved. With an addition of 0.5 % weight CNTs, there was improvement of 24.37 % in ILSS in epoxy based composites and 10.05 % enhancement in thermoplastic polyurethane reinforced glass fibre composites. The average ILSS obtained for thermoplastic polyurethane composites was less than that of epoxy composites. The TPU based composites also demonstrated inelastic deformations without any trace of brittle fracture. The pristine epoxy based composites on the other hand did show inelastic deformations followed by brittle fracture. Higher concentrations of MWCNTs led to an absence of brittle fracture during the tests, owing to the crack bridging effect of the CNTs.
Aakash Ali,Muhammad Ali Nasir,Muhammad Yasir Khalid,Saad Nauman,Khubab Shaker,Shahab Khushnood,Khurram Altaf,Muhammad Zeeshan,Azhar Hussain 대한기계학회 2019 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.33 No.9
Natural fiber composites have great potential for reducing the product cost, lowering weight and enhancing renewability. Functionality and performance of natural fibers can be enhanced many folds using them together with synthetic fibers. Hybridization of carbon and low-cost natural jute fiber offers a sustainable hybrid composite having high modulus and mechanical strength. This study investigates flexural behavior of carbon/jute epoxy composites experimentally and numerically. Also, impact response is characterized through drop weight method. Study concludes that flexural strength decreases with increase in jute percentage. Simulation of flexural behavior diverges more than 10 % from experimental results. This anomaly is due to waviness of fiber resulting in heterogeneous property distribution in composites. Further, the fracto-graphic study revealed modes of failure. The drop weight impact tests reveal increased damage area with increase in jute percentage.