Pootawang, Panuphong,Saito, Nagahiro,Takai, Osamu,Lee, Sang-Yul IOP Pub 2012 Nanotechnology Vol.23 No.39
<P>Arc discharge in solution, generated by applying a high voltage of unipolar pulsed dc to electrodes of Ag and Pt, was used as a method to form Ag/Pt bimetallic nanocomposites via electrode erosion by the effects of the electric arc at the cathode (Ag rod) and the sputtering at the anode (Pt rod). Ag/Pt bimetallic nanocomposites were formed as colloidal particles dispersed in solution via the reduction of hydrogen radicals generated during discharge without the addition of chemical precursor or reducing agent. At a discharge time of 30 s, the fine bimetallic nanoparticles with a mean particle size of approximately 5 nm were observed by transmission electron microscopy (TEM). With increasing discharge time, the bimetallic nanoparticle size tended to increase by forming an agglomeration. The presence of the relatively small amount of Pt dispersed in the Ag matrix could be observed by the analytical mapping mode of energy-dispersive x-ray spectroscopy and high-resolution TEM. This demonstrated that the synthesized particle was in the form of a nanocomposite. No contamination of other chemical substances was detected by x-ray photoelectron spectroscopy. Hence, solution plasma could be a clean and simple process to effectively synthesize Ag/Pt bimetallic nanocomposites and it is expected to be widely applicable in the preparation of several types of nanoparticle. </P>
Pootawang, Panuphong,Kim, Seong Cheol,Kim, Jung Wan,Lee, Sang Yul American Scientific Publishers 2013 Journal of Nanoscience and Nanotechnology Vol.13 No.1
<P>The environmental concern pays much attention to the recent cause of the global warming effect. The reduction of the chemical uses is one of many ways to avoid this crucial problem. Herein, the green process for silver nanometallic particle formation and incorporation in gelatin are proposed. By using a novel discharge process in solution named solution plasma, the silver nanometallic particle formation and its incorporation in gelatin could be accomplished in one-batch reactor during discharge by using silver nitrate (AgNO3) solution as the precursor and controlling systematical parameters. The three-dimensional scaffolds of gelatin/silver biocomposite were fabricated using lyophilizer and the water-soluble property of gelatin was improved by irradiation of ultraviolet ray. The well dispersed silver nanoparticles with the mean particle size 10-20 nm in the good texture of gelatin matrix were obtained. The density of micropore in gelatin/silver scaffold was proportional to the gelatin concentration. In addition, thermal stability of prepared samples had no change comparing with pure gelatin, indicating that the incorporation of silver nanoparticles in gelatin matrix did not affect to the nature of gelatin.</P>