Muhammad Rizwan Dilshad,Atif Islam,Aneela Sabir,Muhammad Shafiq,Muhammad Taqi Zahid Butt,Aamir Ijaz,Tahir Jamil 한국공업화학회 2017 Journal of Industrial and Engineering Chemistry Vol.55 No.-
In this study zinc oxide filled and unfilled polyvinyl alcohol (PVA)/polyethylene glycol (PEG) 600 blended membranes with different degrees of cross-linking (mol%) were prepared using formaldehyde as a crosslinking agent and characterized by FTIR, SEM, TGA, mechanical analysis and permeation testing for CO2 and N2 gases. The effects of synthesis parameters like cross-linking ratio, wt.% PEG content and wt.% zinc oxide content on the membrane characteristics were also investigated. It was found that at 60 mol% degree of cross-linking and 60 wt.% PEG content, the membranes showed maximum CO2/N2 ideal selectivity of 26 and reasonable CO2 permeability of 52.9 Barrers at 25 C and 1.5 bar. It was also found that at 2 wt.% zinc oxide content, membranes showed highest CO2/N2 ideal selectivity of 112.8 and maximum CO2 permeability of 423 Barrers at 25 C and 1.5 bar.