Xiaorui Wang,Shuangling Jin,Rui Zhang,Yan Liu,Jiangcan Wang,Zhen Hu,Wangzhao Lu,Shuo Yang,Minglin Jin,Wenming Qiao,Licheng Ling 성균관대학교(자연과학캠퍼스) 성균나노과학기술원 2019 NANO Vol.14 No.3
Reduced graphene oxide (rGO) aqueous dispersions were synthesized from GO suspensions with hydrazine as reducing agent via a microwave-hydrothermal process in ammonia solution. The rGO films were fabricated by vacuum filtration of above dispersions. When the weight ratio of hydrazine to GO (R N2H4/GO) increases from 0.125 to 9, the dispersion stability of rGO nanosheets in hydrazine/ammonia solution degrades gradually, the surfaces of resultant films become rough from smooth and large interspaces turn up in the transverse section. With the increasing of R N2H4/GO, the C/O atomic ratio and orientation degree of (002) plane of rGO films increase, and the in-plane thermal conductivity also increases, achieving a maximum value of 1056 W/m K when R N2H4/GO is 3.375, then decreases because large interspaces in the rGO film with higher reduction degree greatly limit the thermal transport due to the severe phonon scatterings at the sheets boundaries.