Likui Wang,Shichen Lu,Feng Xie,Hanyu Liu,Jiaping Li,Wei Shang,Zhe Zhang,Yuqing Wen 한국공업화학회 2023 Journal of Industrial and Engineering Chemistry Vol.128 No.-
Aluminum (Al) alloys are used in a wide range of applications due to their advantages. However, theexisting corrosion protection methods have insufficient protection ability and cannot achieve longtermprotection. In this paper, reactive protective film on the surface of aluminum alloys using 1-hydroxyethyl-1,1-diphosphonic acid (HEDP) molecules. Then, Lauric acid/Graphene (LA/rGO) film is usedto prepared on the surface of HEDP film. SEM, XRD, EDS, Raman, XPS and WCA were conducted to analyzephysical and chemical features of coatings. The total resistance of the film reaches 1.0 1020 Xcm2, in asalt spray test using 5wt% NaCl as the corrosion medium, corrosion spots appeared on day 28 with a corrosioninhibition efficiency of 99.99%. Theoretical studies with quantum chemical calculations haveshown that HEDP/LA/rGO composite films can be adsorbed on Al alloy surfaces through P-O-Al and PO-C chemical bonding. The influence of phosphate synergistic effect on the corrosion resistance of theself-assembled superhydrophobic composite film on the surface of 6061 aluminum alloy is discussed. This study presents a scientific and innovative design concept to develop coatings with excellent corrosionprotection for aluminum alloy, and then extend their application to certain areas.
Composition modulation of Cu/Cu2O/CuO nanoparticles supported on carbon for p-nitrophenol reduction
Jia Li,Wei Liu,Yongxin Ding,Likui Liu,Fang Li,Qiming Li 한국화학공학회 2019 Korean Journal of Chemical Engineering Vol.36 No.6
Porous carbon supported Cu/Cu2O/CuO ternary catalysts were fabricated by pyrolysis, in which composition modulation of Cu/Cu2O/CuO was successfully realized by adjusting annealing atmosphere. The correlation between annealing atmosphere and composition of Cu/Cu2O/CuO ternary nanoparticles was deeply investigated. XRD and SEM measurement shows that the composition proportion of Cu/Cu2O/CuO can be effectively controlled by adjusting the annealing atmosphere. HR-TEM and EDS analysis showed that Cu/Cu2O/CuO ternary nanoparticles are highly dispersed into the carbon matrix and harvest more hetero-junction active sites. The effect of Cu/Cu2O/CuO composition on their catalytic activity was investigated in catalytic reduction from p-nitrophenol to p-aminophenol. The experimental result indicated that the catalytic activity of Cu/Cu2O/CuO ternary catalysts exhibits higher catalytic activity than Cu2O/CuO or CuO particles. This work provides a new strategy for synthesizing and modulating porous carbon-supported Cu/Cu2O/CuO ternary nanoparticles.