Noda, Minoru,Kodama, Kazushi,Kitai, Satoshi,Takahashi, Mitsue,Kanashima, Takeshi,Okuyama, Masanori The Korean Institute of Electrical and Electronic 2003 전기전자재료 Vol.16 No.9
A metal-ferroelectric [SrBi$_2$Ta$_2$O$\_$9/ (SBT)-high-k-insulator(PrOx)-semiconductor(Si) structure has been fabricated and evaluated as a key part of metal-ferroelectric-insulator-semiconductor-field-effect-transistor MFIS-FET memory, aiming to improve the memory retention characteristics by increasing the dielectric constant in the insulator layer and suppressing the depolarization field in the SBT layer. A 20-nm PrOx film grown on Si(100) showed both a high of about 12 and a low leakage current density of less than 1${\times}$ 10e-8 A/$\textrm{cm}^2$ at 105 MV/cm. A 400-nm SBT film prepared on PrOx/Si shows a preferentially oriented (105) crystalline structure, grain size of about 130 nm and subface roughness of 3.2 nm. A capacitance-voltage hysteresis is confirmed on the Pt/SBT/PrOx/Si diode with a memory window of 0.3V at a sweep voltage width of 12 V. The memory retention time was about 1 104s, comparable to the conventional Pt/SBT/SiO$\_$x/N$\_$y/(SiO$\_$N/)/Si. The gradual change of the capacitance indicates that some memory degradation mechanism is different from that in the Pt/SBT/SiON/Si structure.