Halide Diker,Gamze Belkıs Durmaz,Hakan Bozkurt,Fatih Yes¸ il,Canan Varlikli 한국물리학회 2017 Current Applied Physics Vol.17 No.4
Graphene oxide (GO) was synthesis by Tour method. Particle size distribution effects of raw graphite on the resulting structural, morphological, optical and electrical properties of GO samples and their poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) composites are studied for the graphite particle distributions of <150, 45e75 and 25e45 mm. It is determined that particle size of raw graphite have an impact on oxidation degree, the chemical nature of oxygen functional groups on GO and it also affects the lateral size of obtained GO. PEDOT:PSS-GO composites are utilized as hole injection layer (HIL) in a solution process blue organic light emitting diode. Presence of GO caused negative differential resistance (NDR) and NDR intensity was decreased with the decrease in lateral size of GO, increase in the graphite particle size and carboxyl% of obtained GO. All PEDOT:PSS-GO composite based devices presented better performance than the bare PEDOT:PSS based reference device. The maximum luminous and external quantum efficiency values of the device that contain HIL of PEDOT:PSS-GO(150) were more than 40% and 50% higher than that of the reference, respectively. Two folds of increase in these performance values were able to be reached with the concentration optimization of GO/150 in PEDOT:PSS.
Halide Diker,Fatih Yes¸ il,Canan Varlikli 한국물리학회 2019 Current Applied Physics Vol.19 No.8
Primary (n-propyl amine, n-PRYLA), secondary (dipropyl amine, DPRYLA) and alcohol (propanol amine, PRPOHA) amine derivatives were used as amine sources in graphene oxide (GO) modification and obtained samples were named as nPRYLA-GO, DPRYLA-GO and PRPOHA-GO, respectively. Modified graphene oxide (mGO) derivatives were doped in poly (3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PH1000) and O2 plasma treatment (70W, 3 min) was applied on the spin casted films. PH1000:mGO films presented high optical transparency values (> 90%) and low resistivity (177–183 Ω/sq). The roughness values were increased especially when the hydrophobic alkyl chain containing DPRYLA-GO and nPRYLA-GO were doped in PH1000. Prepared films were utilized as anode in solution processed blue organic light emitting diode. PH1000:PRPOHAGO anode presented more than 30 nm of decrement in full with at half maximum and 1.6, 1.5 and 1.9 fold enhancements in current, power and external quantum efficiency values, compared to those of ITO anode, respectively.