Enhanced dielectric and nonohmic properties of SrTiO3-modified CaCu3Ti4O12 ceramics
Zhao Jiangpeng,Sun Li,Cao Ensi,Hao Wentao,Zhang Yongjia,Chen Jianbin,Ju Lin 한국물리학회 2022 Current Applied Physics Vol.36 No.-
Dielectric and nonohmic properties of CaCu3Ti4O12 (CCTO) ceramics can be modified by addition of SrTiO3 (STO) in different molar proportions which were fabricated by a modified sol-gel method. XRD results indicated that all modified ceramics showed mixed phase consisting of both CCTO and STO. SEM images and grain size distribution probability also presented the change of microstructure with the addition of STO. The dielectric loss of the CCTO/0.4STO ceramics sintered at 1000 ◦C can be lower than 0.02 in a wide frequency (1 kHz–10 kHz), especially at 1 kHz, the dielectric loss of this sample is as low as 0.012. Furthermore, excellent nonlinear I–V electrical characteristic (high breakdown voltage to 54.15 kV/cm for CCTO/0.4STO sintered at 1000 ◦C) was observed as well. All the results indicated that the addition of STO does improve the dielectric properties and nonohmic characteristics of CCTO ceramics dramatically.
Qing Ni,Li Sun,Ensi Cao,Wentao Hao,Yongjia Zhang,Lin Ju 한국물리학회 2020 Current Applied Physics Vol.20 No.9
(Li1+, Al3+) co-doped Ni0.5Zn0.5Fe2O4 ferrites, Ni0.5-xZn0.5-xLixAlxFe2O4 (x = 0.000, 0.025, 0.050 and 0.100), were synthesized by the sol-gel auto-combustion method. X-ray diffraction (XRD), field emission scanning electronic microscope (FESEM), vibrating sample magnetometer (VSM) and LCR meter were used to investigate the structural, magnetic and dielectric properties. Results of XRD and SEM indicate that both doping amount and calcination temperature play significant roles in crystal structure and grain growth. Also, it can be observed that the saturation magnetization and the coercivity change in a noticeable manner. The Ni0.475Zn0.475Li0.025Al0.025Fe2O4 ferrite sintered at 1200 °C has a relatively low coercivity value (62.93 Oe) and the largest saturation magnetization (110.95 emu/g). Besides, dielectric behavior is also improved by Li1+ and Al3+ co-doping