H_2S의 선택적 산화반응에 미치는 변형된 Zeolite X 촉매의 영향
피준현,이종대,박노국,류시옥,이태진 한국공업화학회 2003 응용화학 Vol.7 No.1
The selective oxidation of hydrogen sulfide was studied over Zeolite X catalysts(Zeolite HX, LiX, NaX, KX) that were prepared by ion exchange method. The acidity sequence of modified Zeolite X catalyst was as follow, Zeolite HX >Zeolite LiX> Zeolite NaX >Zeolite KX.The basicity sequence was reverse of acidity one. For the same conditions (reaction temperature: 225˚c space velocity: 20000h^-1), the conversion of hydrogen sulfide was decreased in Zeolite KX > Zeolite NaX > Zeolite LiX > Zeolite HX order. It was determined that the selective oxidation of hydrogen sulfide was influednced by acidity and basicity. In case of Zeolite NaX catalyst, the yield of element surfer 90% can be obtained at reaction temperature(200), the ratio of O2/H2S (0.5).
H2S의 선택적 산화반응에 미치는 변형된 zeolite X 촉매의 영향
피준현 ( Pi Jun Hyeon ),이종대 ( Lee Jong Dae ),박노국 ( Park No Gug ),류시옥 ( Lyu Si Og ),이태진 ( Lee Tae Jin ) 한국공업화학회 2003 공업화학 Vol.14 No.6
양이온 교환법으로 제조된 zeolite HX, LiX, NaX, KX를 촉매로 이용하여 산도에 따른 H₂S의 선택적 산화 반응 특성을 연구하였다. zeolite X 촉매들에 대한 산도는 zeolite HX > zeolite LiX > zeolite NaX > zeolite KX 촉매 순이며 염기도는 산도의 역순으로 알려져 있다. 반응온도 225℃ 공간 속도(GHSV) 20000 h^(-1)에서 각각의 촉매에 대한 반응특성 실험을 수행한 결과 H₂S 전환율이 zeolite KX ≥ zeolite NaX > zeolite LiX > zeolite HX 촉매 순으로 나타났다. 이는 염기도의 순서와 일치하는 것으로 염기성인 zeolite NaX와 zeolite KX 촉매가 H₂S의 선택적 산화반응에 효과적인 촉매임을 확인하였다. 특히 zeolite NaX와 zeolite KX 촉매 상에서 반응온도 200℃, 몰비(O₂/H₂S) 0.5에서 90% 이상의 우수한 원소 황 수율을 얻었다. The selective oxidation of hydrogen sulfide was studied over the various zeolite X catalysts (zeolite HX, LiX, NaX, KXI that were prepared by ion exchange method. The acidity of various zeolite X catalysts decreased in the following order: zeolite HX > zeolite > LiX > zeolite > NaX > zeolite KX. The basicity of the catalysts was the reverse sequence of the acidity. For the same condition (reaction temperature: 225 ℃. space velocity: 20000 h`)_(l) the conversion of hydrogen sulfide decreased in the following order: zeolite KX ≥ zeolite NaX > zeolite LiX > zeolite HX. It was concluded that the reactivity of zeolite NaX and zeolite KX, base catalysts, was superior than that of zeolite LiX and zeolite HX, which were acid catalysts. Particularly, the yield of sulfur element using zeolite NaX and zeolite KX at the reaction condition (temperature = 200 ℃. O_(2)/H_(2)S mole ratio = 0.5) was over 90%.
이승철,김동현,피준현,류시옥 한국공업화학회 2002 응용화학 Vol.6 No.1
Soot formation of acetylene mixtures diluted with argon was studied behind reflected shock waves by monitoring attenuation of a laser beam in visible(632.8nm) region of the spectrum. Experiments were conducted in the range of 1500~3800K for temperatures, in the range of 0.6~3.3 atm for reflected shock pressures. During the pyrolysis of acetylene, a bell-shaped dependences of soot growth rate, induction time and soot yield were observed. At the same temperature range, an increase in total pressure made induction time short and soot growth rate shifted to lower temperature. Soot growth rate was also proportional to initial concentration of acetylene and they had the maximum value in the temperature range of 2000~2100K.
류시옥,이승철,김동현,피준현,이태진 한국공업화학회 2002 한국공업화학회 연구논문 초록집 Vol.2002 No.0
연소과정에서 생성되는 여러 가지 공해물질 중에서 PM10의 주요 공급원 중의 하나로서 인체에 직·간접적으로 유해한 영향을 미치는 soot의 발생을 억제하기 위한 방법을 개발하기 위하여 그 생성과 관련된 특성을 규명하기 위한 연구를 수행하였다. 일반적으로 아세틸렌은 soot의 중요한 precursor로서 탄화수소연료의 연소에 있어서 중요한 중간체이기 때문에 본 연구에서는 충격관과 레이저 흡수분광법을 사용하여 아세 틸렌이 열분해할 때 생성되는 soot의 형성 유발시간, 생성속도, 생성율 등을 측정하여 soot의 생성특성에 대한 속도론적 연구를 수행하였다. 본 연구를 통하여 현재까지 얻은 실험 데이터들을 분석한 결과. 유발시간은 세 가지 온도범위에서 특징적인 경향을 보였다. 2000 K 까지는 계속 감소하였고, 2000~2200 K 범위에서 최소값을, 그 이상 온도에서 약 2600 K 까지는 증가하다가 2600 K부터는 어느 일정한 값으로 접근 항을 알 수 있었다. 매연형성속도 또한 이와 비슷한 경향을 가졌으며, 압력이 높아질수록 최대값을 가지는 온도는 낮은 쪽으로 약간 이동함을 알 수 있었다.