최훈제 ( Hoon Jae Choi ),최성규 ( Chengkui Cui ),박충훈 ( Chung Hoon Park ),김백중 ( Baek Joong Kim ),이종구 ( Chongku Yi ),강경인 ( Kyung In Kang ) 한국건축시공학회 2013 한국건축시공학회 학술발표대회 논문집 Vol.13 No.2
In this study, effects of supplementary cementitious materials(fly ash, blast furnace slag and waste glass) on drying shrinkage of cement mortar were compared and evaluated. The results showed drying shrinkage of cement mortar using blast furnace slag and waste glass is larger than shrinkage due to capillary pressure, while using fly ash is smaller.
최훈제 ( Choi Hoon-jae ),서태석 ( Seo Tae-seok ) 한국건축시공학회 2017 한국건축시공학회 학술발표대회 논문집 Vol.17 No.2
In this study, the effect of insulation curing for mass concrete wall according to thickness and curing period was evaluated by thermal analysis.
최훈제 ( Choi Hoon-jae ),서태석 ( Seo Tae-seok ) 한국건축시공학회 2016 한국건축시공학회 학술발표대회 논문집 Vol.16 No.2
By Testing restrained shrinkage, it is possible to estimating the cracking tendency of concrete such as time to cracking, tensile stress and tensile creep. In this study, tensile creep properties of concrete under restraint shrinkage were investigation through comparison of specimens that JIS and AASHTO proposed. As a results, tensile creep strains in concrete ring specimens were 15% higher than those in uniaxial specimens.
최훈제 ( Choi Hoon-jae ),서태석 ( Seo Tae-seok ),공민호 ( Gong Min-ho ) 한국건축시공학회 2017 한국건축시공학회 학술발표대회 논문집 Vol.17 No.1
Generally, slump of plain concrete slab is about 120~150mm and slump loss is easy to occur. So, water is added to concrete because this method is convenient for Placing. In order to solve this problem, performance evaluation of concrete using improvement type PC admixture was carried out. Target slump is 210mm and compressive strength is 18MPa. As a result, slump reference value was satisfied 60 minutes after placing and 7-day compressive strength was 21~25MPa.
성능개선형 폴리카르본산계 혼화제를 사용한 콘크리트의 성능평가에 관한 실험적 연구
서태석,최훈제,공민호,Seo, Tae-Seok,Choi, Hoon-Jae,Gong, Min-Ho 한국건축시공학회 2017 한국건축시공학회지 Vol.17 No.5
최근 국내에서 천연골재의 고갈, 수급 불균형 등의 이유로 부순모래를 100% 사용하거나, 내륙 지역의 경우 개답사, 마사토 등과 같은 저품질의 골재를 사용하는 경우가 증가하고 있으며, 높은 흡수율과 점성의 증가로 인하여 작업성 확보를 위해 배합수 량이 증가되는 실정이다. 배합수의 증가로 강도 저하, 건조수축 증가, 블리딩 증가 등에 인한 다양한 품질하자를 유발하게 된다. 특히 지하주차장 무근콘크리트의 경우 표면부와 저면의 수축차의 증가로 인한 컬링이 발생하게 되고, 컬링이 발생한 후에 차량이 통과하게 되면 무근 콘크리트에 균열이 발생하게 된다. 지하 최하층의 경우 배수판 사이를 흐르는 지하수의 유입으로 누수현상도 발생하게 되며, 차량 통행에 따른 소음도 발생할 수 있다. 또한 블리딩 증가로 인한 표면 강도 저하로 박리, 박락 등의 하자가 다발적으로 발생하여 매년 민원과 소송이 증가하고 있다. 따라서 본 연구에서는 이러한 문제를 해결하기 위해서 저품질의 골재가 사용되었을 경우 지하주차장 무근콘크리트의 품질하자를 최소화시키기 위한 성능개선형 PC 혼화제를 개발하였으며, 슬럼프 경시변화, 압축강도, 블리딩, 건조수축 길이변화 시험을 실시하여 일반 준PC 혼화제를 사용한 콘크리트와 비교하였다. 그 결과 경시에 의한 슬럼프의 저하를 최소화시킬 수 있음을 확인할 수 있었으며, 추가적인 가수가 필요 없거나 최소화시킬 수 있으므로 일반 준PC 혼화제를 사용한 콘크리트보다 고품질을 확보할 수 있을 것으로 기대된다. 특히 건조수축량이 20% 정도 감소하여 건조수축균열 및 컬링 제어에 효과적일 것으로 판단된다. Because of the supply-demand problem of aggregate, recently, the construction sites using 100% crushed sand are increasing and the use of low quality aggregate such as farmland sand is increasing too. When the low quality aggregate is used, the various quality defect of concrete such as the strength reduction, the increase of shrinkage and bleeding can be occurred. Therefore, in this study, the performance improvement PC admixture was developed to minimize the quality defect of plain concrete of basement parking area, when the low quality aggregate was used at the plain concrete of basement parking area. The slump loss to elapsed time test, the compressive strength test, the bleeding test and the drying shrinkage test were carried out.
수축저감제를 사용한 콘크리트의 건조수축 예측에 관한 연구
서태석,최훈제,Seo, Tae-Seok,Choi, Hoon-Jae 한국건축시공학회 2016 한국건축시공학회지 Vol.10 No.4
콘크리트 건조수축 균열을 제어하기 위하여 수축저감제(SRA)가 개발되었다. SRA는 콘크리트 미세공극의 표면장력을 작게 하여 수축량을 감소시키며, 콘크리트의 품질향상을 위하여 SRA의 사용이 증가되고 있다. 하지만 건조수축을 예측하기 위한 다양한 모델이 존재함에도 불구하고, SRA의 영향을 고려할 수 있는 예측방법이 아직까지 없는 실정이다. 따라서 SRA 콘크리트의 건조수축에 의해 발생하는 인장응력을 정확히 예측할 수 없고, 콘크리트 구조물의 정량적인 사용성 한계의 검토가 불가능하다. 본 연구에서는 SRA 콘크리트의 정량적인 건조수축 변형률 예측가능성을 제시하기 위하여, 건조수축실험값과 기존 모델에 의한 예측값을 비교하였다. 기존 모델에는 SRA의 영향을 고려할 수 없으므로, 실험결과에 근거하여 SRA 첨가율에 따른 수축저감계수를 도출하였고 기존 모델에 수축저감계수를 적용하여 예측값을 구하였다. 그 결과 AIJ 모델, ACI 모델, GL2000 모델은 ${\pm}10%$의 오차범위 내에서 예측값과 실측값이 전반적으로 양호한 상관관계를 보였지만, CEB-FIP 모델과 B3 모델은 예측값이 실측값을 과소평가 하는 것으로 나타났다. Shrinkage Reducing Agent(SRA) was developed in order to control drying shrinkage cracks in concrete, and the use of SRA is increasing since it can control drying shrinkage cracks and improve the quality of concrete structures. Although there are many types of prediction equations of drying shrinkage strain, there is no prediction method which can consider the effect of SRA up to the present. Therefore, it is impossible to predict the tensile stress generated by drying shrinkage of SRA concrete, and to investigate the quantitative serviceability limit state of SRA concrete. In this study, the drying shrinkage of SRA concrete was investigated by experiment and analysis in order to suggest the predictability of drying shrinkage of SRA concrete. As a result, AIJ model, ACI model, GL2000 model showed there was a correlation between the predicted values and the experimental values within the error range of ${\pm}10%$. However, CEB-FIP model and B3 model underestimated the experimental values.