초임계 유체 염색용 염료에 따른 면 섬유의 염색 특성 : C.I. Disperse orange 155, C.I. Disperse red 167
최현석,김훈민,전태영,Choi, Hyunseuk,Kim, Hunmin,Jeon, Taeyoung 한국염색가공학회 2022 韓國染色加工學會誌 Vol.34 No.2
In this study, the dyeing properties of supercritical fluid dyed cotton fabrics were investigated which use two types of dyes, such as C.I. Disperse orange and C.I. Disperse red 167. Dyeing temperature, pressure and leveling time were equally applied at 130 ℃, 250 bar, and 60 minutes with reference to the related literature, and experiments were performed at concentrations of 0.04, 0.1, 0.4 and 0.8 % o.w.f with different concentrations. Dyeability was confirmed through measurement of washing fastness and color coordinate, and a calibration curve of each dye was drawn up and the absorbance of the residual dye was measured to confirm the amount of residual dye and the dye exhaustion rate at the corresponding concentration. As a result of color difference measurement, as the concentration increased, the L<sup>*</sup> value decreased and the K/S value increased. However, as the concentration increased, the increase in K/S value decreased compared to the input amount, and this tendency was more obvious in C.I. Disperse red 167 than in C.I. Disperse orange 155. The dye exhaustion rate which was calculated by using the amount of residual dye in the pot was also C.I. Disperse orange 155 was 96.16 % and C.I. Disperse red 167 was 94.57 %. However, as the dyeing concentration increased, the dye exhaustion rate decreased, that C.I. Disperse orange was 95.33 % and C.I. Disperse red 167 was 90.63 %. As a result of the washing fastness test for both dyes, dyed samples of which concentrations were 0.4 and 0.8 % o.w.f decreased by 0.5 ~ 1.0 grade. This is predicted because the dye did not completely adhere to the amorphous region of the cotton fiber and the dye simply adsorbed. The fastness to rubbing also maintained at least grade 3-4 up to the 0.1 % o.w.f concentration, but at the concentration of 0.4 % o.w.f or higher, it fell to grade 1 or lower, showing a very poor friction fastness.