표면개질된 영가철 나노입자를 이용한 질산성 질소 제거율 향상에 대한 연구
임태숙 ( Taesook Lim ),조윤철 ( Yunchul Cho ),조장환 ( Changhwan Cho ),최상일 ( Sangil Choi ) 한국환경과학회 2016 한국환경과학회지 Vol.25 No.4
In order to treat groundwater containing high levels of nitrate, nitrate reduction by nano sized zero-valent iron (nZVI) was studied using batch experiments. Compared to nitrate removal efficiencies at different mass ratios of nitrate/Fe0, the removal efficiency at the mass ratio of 0.02% was the highest(54.59%). To enhance nitrate removal efficiency, surface modification of nZVI was performed using metallic catalysis such as Pd, Ni and Cu. Nitrate removal efficiency by Cu-nZVI (at catalyst/Fe0 mass ratio of 0.1%) was 66.34%. It showed that the removal efficiency of Cu-nZVI was greater than that of the other catalysts. The observed rate constant (kobs) of nitrate reduction by Cu-nZVI was estimated to 0.7501 min-1 at the Cu/Fe mass ratio of 0.1%. On the other hand, TEM images showed that the average particle sizes of synthetic nZVI and Cu-nZVI were 40~60 and 80~100 nm, respectively. The results imply that catalyst effects may be more important than particle size effects in the enhancement of nitrate reduction by nZVI.