부유대역 용융응고법으로 제조된 YBa_2Cu_3O_x 산화물초전도체의 미세구조와 전기적 특성
노태형,송정환,장규철,한이섭,김소정,구본급,김호기 대전산업대학교 반도체기술연구소 2000 半導體技術硏究所報 Vol.2 No.-
The YBa_2Cu_3O_x-20 wt% Y_2BaCuO_5 composition designed in YBCO system was synthesized by solid state reaction method. The optimum condition of hot zone temperature and growth rate in floating-zone melt were 1080 ℃ and 2.5 mm/hour, respectively. In samples growth as these condition, the low angel boundaries in grain direction and small amount of amorphous phase known as decreasing characteristics of superconducting materials between grain boundaries in microstructure are investigated by polarized light microscopy on the whole. The critical current density(Jc) at 77k of sample using powder fabricated with no CeO_2 and doped 5 wt%CeO_2 were 8,000 A/㎠(Jc : 561A) and 12,000 A/㎠(Jc: 826A) at 0 T by direct current transport method, respectively.