REBCO 초전도 박막제조를 위한 Fluorine-free MOD 전구체 용액 개발
김병주,임선원,김호진,홍계원,이희균,Kim, Byeong-Joo,Lim, Sun-Weon,Kim, Ho-Jin,Hong, Gye-Won,Lee, Hee-Gyoun 한국초전도학회 2006 Progress in superconductivity Vol.7 No.2
New precursor solution with dichloroacetic acid (DCA) was developed for fabricating high $J_c$ REBCO film. DCA based-precursor solution was coated on $LaAlO_3$(001) substrate by dip coating method. Processing parameters such as oxygen partial pressure, water vapor, ramping rate and pyrolysis temperature were controlled in order to obtain a good epitaxial film. The film with thickness of 0.5 micrometer was obtained by single coating and no crack was observed at calcined films. Oxygen partial pressure was controlled in the range of $100{\sim}1,000$ ppm and conversion heat treatment was carried out at the temperature range of $705-765^{\circ}C$. A critical transition temperature ($T_c$) of 90 K and a critical transport current density ($J_c$) of $>0.5\;MA/cm^2$ (77 K and self-field) were obtained for the GdBCO film. It is thought that fluorine-free MOD solution using DCA is promising precursor solution for fabricating high quality REBCO films.
Deposition of Epitaxial YBCO Films on $LaAlO_3$(100) Substrate by Spray Pyrolysis Method
김호진,주진호,홍석관,이선왕,임선원,이희균,홍계원,Kim Ho-Jin,Joo Jinho,Hong Suk-Kwan,Lee Sun-Wang,Lim Sun-Weon,Lee Hee-Gyoun,Hong Gye-Won The Korean Superconductivity Society 2005 Progress in superconductivity Vol.7 No.1
[ $YBa_{2}Cu_{3}O_y$ ] superconducting films were prepared on $LaAlO_3$(100) single crystal substrate by spray pyrolysis method. The precursor solution was prepared by dissolving nitrate powders in de-ionized water. Both of ultrasonic and concentric nebulizers were used in order to generate fine droplets of precursor solution. C-axis oriented films were obtained at deposition temperature of $750\~850^{\circ}C$ and working pressure of 100 Torr and 500 Torr. In case of ultrasonic nebulizer, films showed rough and porous surface morphology due to formation of enormous droplets, while smooth and dense films were obtained for concentric nebulizer. A transport $J_c$ value of $0.43\;MA/cm^2$ at 77 K and self field was achieved on $LaAlO_3$(100) single crystal substrate.