산업 폐부산물을 혼합재로한 고강도 시멘트 경화체의 제조 및 특성분석
연영훈,최상흘 한국세라믹학회 1994 한국세라믹학회지 Vol.31 No.12
High strength cement hardened body was prepared by ordinary portland cement, silica-fume, super-plasticizer and the industrial by-product powder such as tailing, paper sludge ash and granulated slag. These raw materials were mixed and formed with w/c=0.18. The cement hardened body is cured in the autoclave at 18$0^{\circ}C$, 10atm. These admixtures made the compressive strength of all specimens develope by 170~230%. The highest compressive strength could be obtained by 236 MPa when mix composition was 14 wt% of silica-fume and 26 wt% of granulated slag. The compressive strength increased with decreasing the average pore size and the amount of the poe over the size of 50 nm by which the appearance of high compressive strength of the cement hardened body were mainly influenced. In the result, the hydration products were C-S-H, tobermorite and ettringite and it was realized that the reason why the cement hardened body became dense and revealed the higher strength was that those hydrates were formed inside of the pore and filled in it and the unhydrated materials played the role of an inner-filler.
그래핀 삽입을 통한 구리 후막의 잔류 응력 조절에 관한 연구
박준영,오병문,연영훈 大田大學校 産業技術硏究所 2019 산업기술연구소 論文集 Vol.30 No.1
전기/전자 부품을 이루는 소자의 고밀도화가 진행됨에 따라 이들 부품에서는 많은 열이 발생하게 되었다. 이러한 열은 제품의 피로현상을 나타나게 하며, 이는 수명과 효율을 저하시키는 주된 요인이 되기 때문에 소자에서 발생하는 열을 해소시키는 것이 매우 중요한 문제로 주목받고 있다. 방열 특성이 우수한Metallized Ceramic Substrate의 제조에 필요한 Cu film을 sputtering을 통해 형성하는 경우, 높은 내부 에너지의 플라즈마를 이용하기 때문에 준안정상태에서 막이 성장하게 되어 높은 잔류 응력을 가지게 된다. 결국이로 인해 박막이 갈라지거나 박리와 같은 특성 저하가 나타난다.본 연구에서는 이러한 문제를 해결하기 위해 DC Magnetron Sputtering을 이용한 Cu 후막 제조 공정에서 Cu 층 사이에 이종 물질인 Graphene을 샌드위치 구조로 삽입하여 잔류 응력을 제어하고자 하였다.