http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
저압화학기상성장법으로 제작된 SixOyNz 의 알칼리이온 감지성에 관한 연구
신백균,이덕출 ( P . K . Shin,D . C . Lee ) 한국센서학회 1997 센서학회지 Vol.6 No.3
Using SiC1₂H₂, NH₃ and N₂O, we have fabricated silicon oxynitride (Si_xO_yN_z) layers on thermally oxidized silicon wafer by low pressure chemical vapor deposition. Three different compositions were achieved by controlling gas flow ratios(NH₃/N₂O) to 0.2, 0.5 and 2 with fixed gas flow of SiC1₂H₂. Ellipsometry and high frequency capacitance-voltage(HFCV) measurements were adapted to investigate the difference of the refractive index, dielectric constant, and composition, respectively. Regardless of nitride content, silicon oxynitrides had similar stability to silicon nitrides. The relative standing of alkali ion sensitivity in silicon oxynitride layers was influenced by nitride content. The better alkali ion-sensitivity was achieved by increasing oxide content in bulk of silicon oxynitrides.
터널링 박막 두께 변화에 따른 부동 게이트 유기 메모리 소자
김희성,이붕주,신백균,Kim, H.S.,Lee, B.J.,Shin, P.K. 한국진공학회 2012 Applied Science and Convergence Technology Vol.21 No.6
유기 메모리 절연막 제작을 위해 일반적으로 사용되어지는 습식법이 아닌 건식법 중 플라즈마 중합법을 이용하였다. 유기 절연 박막으로 사용된 단량체는 Styrene과 MMA을 사용하고, 터널링 박막은 MMA를 사용하며, 메모리 박막은 열기상증착법을 이용한 Au 박막을 사용하였다. 최적화된 소자의 구조는 Au의 메모리층의 두께를 7 nm, Styrene 게이트 절연막의 두께를 400 nm, MMA 터널링 박막의 두께를 30 nm로 증착하여 제작된 부동 게이트형 유기 메모리 소자는 40/-40 V의 double sweep시 27 V의 히스테리시스 전압을 얻을 수 있었다. 이 특성을 기준하여 유기 메모리의 전하 포집 특성을 얻을 수 있었다. 유기 재료 중 MMA 대비 Styrene의 전하 포집 특성이 좋은 것으로 보아 향후 부동 게이트인 Au 박막을 유기 재료인 Styrene으로 대체하여 플렉시블 소자의 가능성을 기대한다. The organic memory device was made by the plasma polymerization method which was not the dry process but the wet process. The memory device consist of the styrene and MMA monomer as the insulating layer, MMA monomer as the tunneling layer and Au thin film as the memory layer which was fabricated by thermal evaporation method. The I-V characteristics of fabricated memory device got the hysteresis voltage of 27 V at 40/-40 V double sweep measuring conditions. At this time, the optimized structure was 7 nm of Au thin film as floating gate, 400 nm of styrene thin film as insulating layer and 30 nm of MMA thin film as tunneling layer. Therefore we got the charge trapping characteristics by the hysteresis voltage. From the paper, styrene indicated a good charge trapping characteristics better than MMA. In the future, we expect to make devices by using styrene thin film rather than Au thin film.
TCP-CVD법을 활용한 공정변수에 따른 산화막의 제작
김창조,최윤,신백균,박구범,신현용,이붕주,Gim, T.J.,Choi, Y.,Shin, P.K.,Park, G.B.,Shin, H.Y.,Lee, B.J. 한국진공학회 2010 Applied Science and Convergence Technology Vol.19 No.2
본 논문에서는 유기발광다이오드의 보호막 적용을 위하여 TCP-CVD를 이용한 실리콘 산화막 형성에서 산화막의 특성에 영향을 미치는 Power, 가스종류 및 유량, 소스와 기판거리 및 공정온도 등의 공정조건에 따른 증착된 산화막의 특성을 나타내는 증착률, 굴절률을 제어하고자 한다. 그 결과 $SiH_4$ : $O_2$ = 30 : 60 [sccm], 70 [mm]의 source와 기판 거리, Bias를 인가하지 않은 조건에서 80 [$^{\circ}C$] 이하의 공정온도를 보였으며 투과율 90% 이상, 높은 증착률 및 굴절률 1.4~1.5인 안정된 $SiO_2$ 산화박막을 제조할 수 있었다. We have fabricated $SiO_2$ oxidation thin films by TCP-CVD (transformer coupled plasma chemical vapor deposition) method for passivation layer of OLED (organic light emitting diode). The purpose of this paper is to control and estimate the deposition rate and refracive index characteristics with process parameters. They are power, gas condition, distance of source and substrate and process temperature. The results show that transmittance of thin films is over 90%, rapid deposition rate and stable reflective index from 1.4 to 1.5 at controled process conditions. They are $SiH_4$ : $O_2$ = 30 : 60 [sccm] gas condition, 70 [mm] distance of source and substrate, no-biased substrate and under 80 [$^{\circ}C$] process temperature.