The basis for determining hearing disturbance adopted by the Life Insurance Industry is the loss of hearing power above 80 db on either or both sides, in accordance with the divide sixth method of audiometric test. Different types of small-to-medium-sized enterprises were chosen for the study of the extent of loss and the power of hearing. The following are the findings: 1. The disturbance percentage found among the types of occupation and different levels of age was found to be higher as the subject's ages increased. 2. The heavier the workload and the noisier the environment, the higher the percentage of disturbance. The average percentage of the subjects turned out to be 24.35%. Those engaged in sawing and wood-work showed 49%. Those engaged in machinery and equipment for transportation accounted for 42.6%. Those engaged in the metal products occupied 39.6%. The disturbance percentage among those engaged in such noisy works as press, pipe and sawing showed 32.52%. 28.46% of those workers with three to four years employment turned out to be disturbed in hearing. Of these, a high percentage of 43.9% showed disturbance in conversation or talk. 3. No hearing loss due to occupation beyond the Life Insurance standard of 80 db was found; therefore, the present status poses no problem. Constant attention, however, is needed.
전착법을 이용한 CuInSe<sub>2</sub> 박막태양전지 광활성층의 조성 조절
박영일,김동환,서경원,정증현,김홍곤,Park, Young-Il,Kim, Donghwan,Seo, Kyungwon,Jeong, Jeung-Hyun,Kim, Honggon 한국전기전자재료학회 2013 전기전자재료학회논문지 Vol.26 No.3
Thin light-active layers of the $CuInSe_2$ solar cell were prepared on Mo-coated sodalime glass substrates by one-step electrodeposition and post-annealing. The structure, morphology, and composition of $CuInSe_2$ film could be controlled by deposition parameters, such as the composition of metallic precursors, the concentration of complexing agents, and the temperature of post-annealing with elemental selenium. A dense and uniform Cu-poor $CuInSe_2$ film was successfully obtained in a range of parametric variation of electrodeposition with a constant voltage of -0.5 V vs. a Ag/AgCl reference electrode. The post-annealing of the film at high temperature above $500^{\circ}C$ induced crystallization of $CuInSe_2$ with well-developed grains. The KCN-treatment of the annealed $CuInSe_2$ films further induced Cu-poor $CuInSe_2$ films without secondary phases, such as $Cu_2Se$. The structure, morphology, and composition of $CuInSe_2$ films were compared with respect to the conditions of electrodeposition and post-annealing using SEM, XRD, Raman, AES and EDS analysis. And the conditions for preparing device-quality $CuInSe_2$ films by electrodeposition were proposed.