Voltage Applicable to $Au/YBa_2Cu3O_7$ Meander Lines
김혜림,임성우,유승덕,박충렬,양성은,김우석,현옥배,Kim, H.R.,Yim, S.W.,Yu, S.D.,Park, C.R.,Yang, S.E.,Kim, W.S.,Hyun, O.B. The Korean Superconductivity Society 2010 Progress in superconductivity Vol.12 No.1
We investigated the voltage applicable to $Au/YBa_2Cu3O_7$ (YBCO) meander lines. The meander line was fabricated by patterning Au/YBCO thin films grown on sapphire substrates by photolithography. It was subjected to simulated AC fault currents, and the resistance was measured and analyzed. The samples were immersed in liquid nitrogen during the experiment for effective cooling. The voltage applicable to the meander lines depended on the fault duration. Dependence was strong at short fault durations, and weak at long durations. When the voltage was plotted as a function of the fault duration on a log-log scale, data fell more or less on straight lines for all meander lines. In other words, the voltage applicable to Au/YBCO meander lines on sapphire substrates was inversely proportional to $t^b$, where t is the fault duration and b ranges from 0.4 to 0.5. The results were analyzed quantitatively with the concept of heat balance. Under adiabatic condition, the voltage is to be inversely proportional to $t^{0.5}$ for all samples. Less value of b for some samples is thought to be due to cooling of the samples by liquid nitrogen.
Temperature Behavior of Superconducting Fault Current Limiters during Quenches
김혜림,심정욱,현옥배,Kim H.-R.,Sim J.,Hyun O.-B. The Korean Superconductivity Society 2005 Progress in superconductivity Vol.6 No.2
We investigated temperature behavior of superconducting fault current limiters (SFCLs) during quenches. Knowledge on temperature behavior during quenches is important to the design of SFCLs, because the temperature of SFCLs is related to their stability. SFCLs were fabricated by patterning $Au/YBa_2Cu_3O_7$ thin films grown on sapphire substrates into meander lines by photolithography. A gold film grown on the back side of the substrate was patterned into a meander line, and used as a temperature sensor. The front meander line was subjected to simulated AC fault currents, and the back line to DC current. They were immersed in liquid nitrogen during the experiment for effective cooling. Overall, temperature at the back side of SFCLs was close to that at the front side. It was closer at the beginning of faults, and at lower applied voltages. Temperature distribution at the back side was even except at the edge, as at the front side. These results tell that the whole SFCL was heated to similar degree during quenches, and that effective cooling of SFCLs at the back side is as important to the stability of SFCLs as at the front side. The results could be explained with the concept of heat transfer within the film.
Quench Development in Coated Conductors
김혜림,박충렬,임성우,유승덕,오성용,현옥배,Kim, H.R.,Park, C.R.,Yim, S.W.,Yoo, S.D.,Oh, S.Y.,Hyun, O.B. The Korean Superconductivity Society 2009 Progress in superconductivity Vol.10 No.2
We measured and analyzed the quench development in coated conductor(CC) tapes. The CC was grown on hastelloy substrates and has an Ag protection layer. The tapes were subjected to simulated AC fault currents for quench development measurement. They were immersed in liquid nitrogen during the experiment. The quench resistance increased rapidly first, and the increase slowed down afterwards. It increased linearly with applied voltage at lower voltages, and depended less strongly on applied voltage at higher voltages. The resistance was compared with that of Au/YBCO films grown on sapphire substrates, and found to increase more monotonously than the latter. Data were analyzed quantitatively with the concept of heat transfer within the tape and the surrounding liquid nitrogen. A heat balance equation was derived and solved, taking into consideration temperature dependence of thermal parameters of the tapes. Solutions, together with values of thermal parameters taken from the literature, explained the data well. Cooling by liquid nitrogen affected the quench development considerably at lower applied voltages. Dependence on applied voltages could be also understood quantitatively.
김혜림,임성우,오성용,현옥배,Kim, H.R.,Yim, S.W.,Oh, S.Y.,Hyun, O.B. 한국초전도학회 2008 Progress in superconductivity Vol.9 No.2
We investigated the size effect on quench development in $Au/YBa_2Cu_3O_7$ (YBCO) thin film meander lines on sapphire substrates. The meander lines were fabricated by patterning YBCO films coated with gold layers. The lines were subjected to simulated AC fault current, and immersed in liquid nitrogen during the experiment. After the initial rapid rise, the resistance increased moderately and then slowly. In 4 inch-diameter meander lines, the period during which the resistance increased moderately was considerably longer than in 2 inch-diameter line. Moderate increase of resistance was originated from quench propagation. The film temperature was about 180 K at the point when the propagation was completed. The rate of resistance increase after the quench completion was not affected by the film size.
Analysis on Recovery in Au/YBCO thin Film Meander Lines
김혜림,임성우,오성용,현옥배,Kim, H.R.,Yim, S.W.,Oh, S.Y.,Hyun, O.B. The Korean Superconductivity Society 2007 Progress in superconductivity Vol.9 No.1
We investigated recovery in $Au/YBa_2Cu_3O_7$ (YBCO) thin film meander lines on sapphire substrates. The meander lines were fabricated by patterning YBCO films coated with gold layers. The lines were subjected to simulated AC fault current and then small current was applied for recovery measurements. The samples were immersed in liquid nitrogen during the experiment. After the fault, the resistance decreased linearly, first slowly and then fast to zero. The initial slow decrease was due to the decrease of the meander line temperature, whereas the fast decrease was originated from the transition from the normal state to the superconducting state. The recovery speed depended on the size of samples, and was faster in the smaller samples during the whole period of recovery. The experimental results were analyzed quantitatively with the concept of heat transfer within the sample and to the surrounding liquid nitrogen. A heat balance equation was solved for the initial phase of recovery, and an expression for the time dependence of resistance was obtained. The result agreed with data well.
Resistance Development in Au/YBCO Thin Film Meander Lines under High-Power Fault Conditions
김혜림,심정욱,최인지,임성우,현옥배,Kim, H.R.,Sim, J.,Choi, I.J.,Yim, S.W.,Hyun, O.B. The Korean Superconductivity Society 2006 Progress in superconductivity Vol.8 No.1
We investigated resistance development in $Au/YBa_2Cu_3O_7(YBCO)$ thin film meander lines during high-power faults. The meander lines were fabricated by patterning 300 nm thick YBCO films coated with 200 nm thick gold layers into meander lines. A gold film grown on the back side of the substrate was also patterned into a meander line. The front meander line was connected to a high-power fault-test circuit and the back line to a DC power supply. Resistance of both lines was measured during the fault. They were immersed in liquid nitrogen during the experiment. Behavior of the resistance development prior to quench completion could be understood better by comparing resistance of the front meander lines with that of the back. Quench completion point could be determined clearly. Resistance and temperature at the quench completion point were not affected by applied field strength. The experimental results were analyzed quantitatively with the concept of heat transfer within the meander lines/substrate and to the surrounding liquid nitrogen. In analysis, the fault period was divided into three regions: flux-flow region, region prior to quench completion, and region after quench completion. Resistance was calculated for each region, reflecting the observation for quench completion. The calculated resistance in three regions was joined seamlessly and agreed well with data.
YBCO 박막을 이용한 3상 6.6kV 항형 초전도 한류기의 동시Quench 분석
심정욱,김혜림,현옥배,Sim J,Kim H. R,Hyun O. B 한국초전도학회 2004 Progress in superconductivity Vol.6 No.1
We fabricated a resistive type superconducting fault current limiter (SFCL) of 3-phase $6.6 kV_{rms}$ / rating, based on YBCO thin films grown on sapphire substrates with a diameter off inch. Each element of the SFCL was designed to have the rated voltage of $600 V_{rms}$ $/35A_{rms}$. The elements produced a single phase with 8${\times}$6 components connected in series and parallel. In addition, a NiCr shunt resistor of 23 $\Omega$ was connected in parallel to each of them for simultaneous quenches between the elements. Prior to investigating the performance of the 3 phase SFCL, we examined the quench characteristics for 8 elements connected in series. For all elements, simultaneous quenches and equal voltage distribution within 10% deviation from the average were obtained. Based on these results, performance of the SFCL for single line-to-ground faults was investigated. The SFCL successfully limited the fault current of $10 kA_{ rms}$ below 816 $A_{peak}$ within 0.12 msec right after the fault occurred. During the quench process, average temperature of all components did not exceed 250 K, and the SFCL was totally safe during the whole operation.