Sol-Gel법에 의한$ZrO_2$ Ceramic Fiber 제조
김선욱,김성숭,W.C. LaCourse 한국세라믹학회 1990 한국세라믹학회지 Vol.27 No.6
Zirconia gel fibers were fabricated by sol-gel processing using zirconium alkoxides and 2, 4-pentanedione. Their phase transformation and microstructural evolution were studied after heat treatments up to 150$0^{\circ}C$. Tetragonal ZrO2 began to form at 50$0^{\circ}C$ and followed by monoclinic, tetragonal phase during subsequent heat treatments at 1000, 150$0^{\circ}C$ for 1hour respectively. During cooling from 150$0^{\circ}C$, cracks were created, propagated along grain boundaries due to the volume change from tetragonal to monoclinic transformation.
Sol-Gel Processing에 의한 순수 $PbTiO_3$ Ceramics 제조
김선욱,윤만순,임종인,김성숭,김남흥 한국세라믹학회 1992 한국세라믹학회지 Vol.29 No.3
Crack free PbTiO3 ceramics were produced by sol-gel processing using alkoxide, which has not been reported to be successful. The PbTiO3 gels were prepared from Ti alkoxide and lead acetate without any dopants. They were calcined at $600^{\circ}C$ and miled to produce fine PbTiO3 powder. It was pressed into discs and they were sintered at 110$0^{\circ}C$ for a few hours. The sintered ceramics were relativley hard and dense as having about 96% of theoretical density of PbTiO3. Fabrication of pure PbTiO3 ceramics by sol-gel processing is possibly due to their small grain size and uniform distribution of residual stress created during cubic-tetragonal transition over large number of small grains in fine grain PbTiO3 ceramics.