김상섭,이온영,이철규,전병세 한국세라믹학회 1994 한국세라믹학회지 Vol.31 No.4
Compacts were prepared using the SHS(Self-propagating High-temperature Synthesis) method and nitrided at temperatures range from 145$0^{\circ}C$ to 175$0^{\circ}C$, and pressed at 180$0^{\circ}C$ under N2 atmosphere. The samples were characterized for bulk density, porosity, pore size and distribution, phase composition, microstructure and fracture toughness. Compacts were composed of whiskers, which showed a good candidate for the composite materials. The major phases of the compacts nitrided at 175$0^{\circ}C$ and pressed at 180$0^{\circ}C$ were 15R-sialon with a large aspect ratio.
스퍼터링 증착에 의한 $PbTiO_3$ 박막제조시 증착변수의 영향
김상섭,강영민,백성기 한국세라믹학회 1993 한국세라믹학회지 Vol.30 No.7
Highly c-axis oriented ferroelectric PbTiO3 thin films were deposited on MgO single crystal substrates by RF magnetron sputtering. We have studied the effects of substrate temperature, RF input power, gas comosition, gas pressure and deposition rate on the chemical and structural characteristics of PbTiO3 thin films. The epitaxy relationship of c-axis oriented films was found to be PbTiO3{100}//MgO(100) and their microstructures were highly mosaic. It was found that the most important parameter to achieve epitaxial PbTiO3 films was the substrate temperature. The activation energy for the epitaxy formation was about 0.92eV. Lower gas pressure and RF input power were favorable for the formation of epitaxial c-axis orientation. It was also found that the optimum oxygen content in Ar gas was 10% to obtain the stoichiometric PbTiO3 composition.