This paper focuses on the sterilization of Escherichia coli (E. coli) by using dielectric barrier discharge (DBD) plasma. The death rate of E. coli was evaluated by changing the electric power and treatment time under various conditions, i.e., with ultraviolet alone, with ozonation alone, and with ultraviolet plus ozonation.
니켈/알루미나 촉매상에서 CO의 플라즈마 촉매 메탄화 반응에 미치는 니켈 함량의 영향
좌은진 ( Eun Jin Jwa ),장두일 ( D. I. Jang ),고란영 ( R. Y. Ko ),이상백 ( S. B. Lee ),목영선 ( Y. S. Mok ) 한국공업화학회 2011 응용화학 Vol.15 No.1
알루미나에 0∼12.5%의 니켈이 담지 된 촉매와 플라즈마를 결합하여 일산화탄소의 촉매 메탄화 반응을 수행하였다. CO와 H2는 1:3의 비율로 반응기에 유입되었으며 H2, CO, CO2, CH4의 농도는 가스 크로마토그래피로부터 측정되었다. 알루미나(bare alumina)를 사용하였을 때는 CO가 CH4로 전환되지 않았지만 니켈이 담지 된 촉매는 메탄화 반응에 영향을 주었고, 촉매상의 니켈 조성이 증가함에 따라 반응 속도가 증가되었다. 저 농도의 니켈이 함량된 촉매를 사용했을 경우 300℃ 이상의 고온에서 반응을 진행했을 경우에는 촉매 자체의 활성이 높아 거의 최대 효율을 나타냈다. 240℃ 이하의 저온영역에서는 다소 메탄화 효율이 낮았지만 저온 플라즈마에 의해 CO와 H2가 들뜬 상태로 활성화되어 촉매적 메탄화 효율은 증가하였다. 고 농도의 니켈이 함량된 촉매를 사용한 반응에서는 촉매 자체의 활성이 저온영역에서 좋았으나 저온플라즈마에 의해 더욱 메탄화 반응이 향상되었다.
플라즈마 소수성 코팅을 이용한 실리케이트계 황색형광체의 내구성 개선에 관한 연구
목영선 ( Young Sun Mok ),장두일 ( Doo Il Jang ),조진오 ( Jin Oh Jo ),고란영 ( Ran Young Ko ),이상백 ( Sang Baek Lee ) 한국화학공학회 2013 Korean Chemical Engineering Research(HWAHAK KONGHA Vol.51 No.2
Hydrophobic coating on a silicate-based yellow phosphor (Sr2SiO4:Eu2+) was carried out by using hexamethyldisiloxane (HMDSO) precursor in an atmospheric pressure dielectric barrier discharge plasma reactor, eventually to improve the long-term stability and reliability of the phosphor. The phosphor powder samples were characterized by a scanning electron microscope (SEM), a transmission electron microscope (TEM), a fluorescence spectrophotometer and a contact angle analyzer. After the coating was prepared, the contact angle of the phosphor powder increased to 133.0o for water and to 140.5o for glycerol, indicating that a hydrophobic layer was formed on its surface. The phosphor coated with HMDSO exhibited photoluminescence enhancement up to 7.8%. The SEM and TEM images of the phosphor powder revealed that the plasma coating led to a morphological change from grain-like structure to smooth surface with 31~46 nm thick hydrophobic layer. The light emitting diode (3528 1 chip LED) fabricated with the coated phosphor showed a substantial enhancement in the reliability under a special test condition at 85 oC and 85% relative humidity for 1,000 h (85/ 85 testing). The plasma-mediated method proposed in this work may be applicable to the formation of 3-dimensional coating layer on irregular-shaped phosphor powder, thereby improving the reliability.