계용찬,손낙진,권오대 대한전자공학회 1994 전자공학회논문지-A Vol.31 No.10
Gain-guided broad-area single quantum well separate confinement heterostructure diode lasers have been fabricated from structures grown by metal organic vapor phase epitaxy. The active layer of the epi-structure is InGaAs emitting 962-965nm and the guiding layer GaAs. The channel width is fixed to 150${\mu}$m and the cavity length varys within the range of 300~800${\mu}$m. For uncoated LD's, the output power of 0.7W has been obtaained at a pulsed current level of 2A, which results about 60% external quantum efficiency. The threshold current density is 200A/cm$^{2}$ for the cavity lengths of 800.mu.m LD's. The stain effect upon the transparent current density has been observed. The internal quantum efficiency is expected to be 88% and the internal loss to be 18$cm^{-1}$. The beam divergence has been measured to be 7$^{\circ}$to lateral and 40$^{\circ}$to transverse direction. finally, 1.2W continuous-wave output power has been obtained at a current level of 2A for AR/HR coated LD's die-bonded on Cu heat-sink and cooled by TEC.
고출력 $Al_{0.07}$$Ga_{0.93}$As 레이저 다이오드 어레이 제작
손노진,박성수,안정작,권오대,계용찬,정지채,최영수,강응철,김재기 대한전자공학회 1995 전자공학회논문지-A Vol.32 No.10
A laser diode(LD) structure consisting of a single 150$\AA$ $Al_{0.07}$Ga$_{0.93}$As quantum well active region operating at ${\lambda}$=809nm, cladded with an AlGaAs graded-index separate confinement heterostructure, has bes been grown by MOCVD. Temperature coefficient of wavelength is approximately 0.2nm $^{\circ}C$ for the diode. The active aperture consists of five emitters separated from each other by means of SiO$_{2}$ deposition and stripe formation, which creates insulating regions that channel the current to 100-$\mu$m-wide stripes placed on 450-$\mu$m centers. From a typical uncoated LD, the output power of 0.8W has been obtained at a 1$\mu$s, 1kHz pulsed current level of 2.0$\AA$, which results in about 64% external quantum efficiency. The threshold current density is 736A/cm$^{2}$ for the case of 500$\mu$m cavity length LD's. The measure of an internal quantum efficiency was 75.8% and the internal loss 4.83$cm^{-1}$ . Finally, 3.1W output power has been obtained at a 1$\mu$s, 1kHz pulsed current level of 9A from the 500$\mu$m-aperture LD array with 460-$\mu$m- cavity length.