선택추출법에 의한 고황산염슬래그 시멘트의 수화반응속도의 측정
송종택,대문정기(大門正機) 한국세라믹학회 1982 한국세라믹학회지 Vol.19 No.1
The technique to determine the components in the supersulphated slag cement is discussed by several selective extraction analyses. Accordingly, the rate of hydration reaction of supersulphated slag cement could be quantitatively measured by the following 3 kinds of the selective extraction analyses. (1) Determination of unreacted slag - a salicylic acid, acetone.methanol solution (2) Determination of free $CaSO_4$ - a half saturated lime water (3) Determination of free $Ca(OH)_2$ - glycerine.alcohol solution
광물질 혼합재와 고유동화제를 첨가한 시멘트 페이스트의 유동특성
송종택,신진호,Song, Jong-Taek,Shin, Jin-Ho 한국세라믹학회 2005 한국세라믹학회지 Vol.42 No.11
Rheological properties of ordinary portland cement (OPC) containing metakaoline (MK), granulated blast furnace slag (GBS) and polycarboxylate type superplasticizer (PCA) were investigated using a mini-slump test, sedimentation test and viscometer. Fluidity of cement pastes containing MK (OPC-MK, OPC-MK-GBS systems) with PCA were higher than those of the cement pastes without MK(OPC, OPC-GBS systems). Colloid suspensions with $0.1\%$ PCA were changed from stable sedimentation behaviors to flocculation behaviors in the OPC-MK, OPC-GBS and OPC-MK-GBS systems. The colloid suspensions showed stable sedimentation behaviors with PCA greater than $0.2\%$. The OPC system showed shear thinning behavior. However, the other systems showed weak shear thinning behaviors with PCA. Rheological properties of cement pastes were improved when MK and GBS were contained together. The rheological properties of OPC-MK, OPC-GBS and OPC-MK-GBS systems were improved by PCA added greater than $0.2\%$.
고로슬래그 및 플라이 애시 분말을 혼합한 시멘트 페이스트의 유동특성
송종택,박효상,변승호,유동우,Song, Jong-Taek,Park, Hyo-Sang,Byun, Seung-Ho,Yoo, Dong-Woo 한국세라믹학회 2008 한국세라믹학회지 Vol.45 No.6
Rheological properties of cement pastes containing blast furnace slag (BFS: 3,900, $7,910\;cm^2/g$) or fly ash powder (FA: 4,120, $8,100\;cm^2/g$) according to the ratio of water/binder (W/B) and the dosage of polycarboxylate type superplasticizer (PC) were investigated by a mini slump and a coaxial cylinder viscometer. In this experiment, the ratio of replacing OPC with BFS or FA was 30 wt%, the W/B was from 30 to 70 wt%. As a result, the fluidity of cement paste containing BFS or FA was improved with increasing W/B and the dosage of PC. BFS or FA replaced cement paste with W/B 70% and PC 0.3% showed the highest fluidity. The segregation range of cement paste was occurred below $10\;d/cm^2$ of the yield stress and below 50 cPs of the plastic viscosity by the coaxial cylinder viscometer. And also it was formed that the plastic viscosity and the yield stress of FA replaced cement paste were higher than them of BFS replaced cement paste.
고로슬래그 분말도가 시멘트 페이스트의 유동특성에 미치는 영향
송종택,유창달,변승호 한국세라믹학회 2007 한국세라믹학회지 Vol.44 No.2
In this study, the rheological properties of cement pastes containing blastfurnace slag of different fineness were investigated. The fluidity of cement pastes with low Blaine value blastfurnace slag was increased with decreasing the plastic viscosity and the yield stress of pastes. And the optimum dosage of polycarboxylate type superplasticizer to the cement pastes was confirmed according to the fineness and the replacement ratio of blastfurnace slag. All cement pastes showed the thixotropy behavior. And also it was formed that the segregation range of cement pastes was occurred below 10 D/cm2 of the yield stress and below 350 cPs of the plastic viscosity by the coaxial cylinder viscometer.
송종택,안민선,정문영 한국세라믹학회 1996 한국세라믹학회지 Vol.33 No.12
In order to investigate the reaction in the system of fly ash-sulfuric acid-calcium hydroxide the hydrates were produced by the addition of Ca(OH)2 to fly ash activated with sulfuric acid at various temperatures. And then they were characterized by XRD. SEM and TG-DTA. It was found that in the reaction of fly ash with sulfuric acid fly ash was not decomposed but Al2O3 and SiO2 component in it were activated. The addition of calcium hydroxide into this system resulted in the formation of ettringite and calcium silicate hydrate (C-S-H) As the concentration of sulfuric acid and reaction temperature increased the amount of calcium hydroxide decreased fast. At this time gypsum produced by the reaction calcium hydroxide with sulfuric acid was consumed to form ettringite. Accordingly the formation of ettringite increased with calcium hydroxide and reaction time. And it showed faster than the formation of C-S-H.
송종택,윤성대,류동우,한경섭 한국세라믹학회 1996 한국세라믹학회지 Vol.33 No.7
Utilization of fly ash by-produced from coal fired power plants and classified as general waste became very important problem to solve in the environmental protection and recycling of waste materials. The possibility of large scale substitution of fly ash as a raw material for bricks and wet tiles was highly expected because the chemical compositions of fly ash were mostly Al2O3 and SiO2 and the properties of it were very similar with clay. Accordingly in order to investigate the substitutional limit these specimens were substituted from 0 to 100 wt% fly ash by 20wt% increment for clay. Fly ash-clay bodies were fired at 1200, 1250 and 130$0^{\circ}C$ and then their properties were measured, It was found that these specimens sintered at 125$0^{\circ}C$ had a good bending strength. Especially when these sintered bodies were added to 20, 40 and 60 wt% fly ash the bending strength of those were 201 , 205 and 191kg.cm2 respectively with the water absorption below 1%, This showed that fly ash could be substituted ab 60 wt% in this experiment.
$CaSO_4$ 자극에 의한 고로수쇄 슬래그의 수화반응
송종택 한국세라믹학회 1980 한국세라믹학회지 Vol.17 No.4
In order to clarify the mechanism of the hydration of supersulphated slag cement, the experiments of suspension hydration were performed in the mixtures of slag+CaSO4+water or NaOH solutions with a liquid/solid ratio of 10. The liquid and solid phase of the suspension was chemically analysed and discussed. In the slag-$CaSO_4$--NaOH system, $Al_2O_3$ was dissolved under high pH condition, and the ettringite was formed by a reaction of $CaSO_4$ and $Al_2O_3$ released in the solution. As hydration progressed, ettringite coated the surface of unhydrated slag grains and inhibited the hydration reaction of slag. $CaSO_4$ was not only an activator for slag hydration, but a reactant in the hydration.
송종택,대문정기(大門正機),근등련일(近藤連一) 한국세라믹학회 1980 한국세라믹학회지 Vol.17 No.3
The experiments of suspension hydration were performed in the mixtures of slag and water or NaOH solutions which were made up with a liquid/solid ratio of 10. The liquid phase of the suspension was chemically analysed and discussed. When slag was in contact with water, CaO component was released from slag grains into the solution. The amounts of $SiO_2$ and $Al_2O_3$ liberated in the solution were very low as compared with CaO, for the impermeable coating of $SiO_2$, $Al_2O_3$-rich gel was formed on the surface of slag grains. The hydration was considered to be inhibited by this impermeable coating. The weak hydraulic property of slag was based on slowly released CaO and dissolved Na, K components which increased pH in the solution.