스피넬계 흑색 안료를 이용한 흑색 지르코니아 세라믹스의 제조 및 특성분석 = Preparation and Characterization of Black Zirconia Ceramics by Black Color Spinel Pigment

다국어 초록 (Multilingual Abstract)

The zirconia ceramics are widely used because of their excellent mechanical properties. Recently, many researches to make a colored zirconia was achieved to satisfy the individual aesthetic requirements. In this study, the synthesis of black-color spinel-based inorganic pigments which are stable above $1400^{\circ}C$ and the fabrication of black-colored zirconia using the synthesized pigments are investigated. Inorganic pigments which have spinel structure and near black color were synthesized by a solid state reaction method using a $Fe_2O_3,\;Cr_2O_3$, CoO and NiO powder as a starting materials at $1600^{\circ}C$. Most of synthesized pigments were black colored spinel phases and single spinel phase was successfully synthesized at the composition range of $Cr_2O_3:25{\sim}35%,\;Fe_2O_3:45{\sim}55%$, CoO:20% and NiO:$6{\sim}10%$. The black-colored zirconia was fabricated at $1410^{\circ}C$ with the 5 wt% synthesized pigments and their properties were evaluated. The results showed that the strength value was more than 848 MPa, absorption rate was 0.1%, the brightness of color was $L^*:40{\sim}42$, the tone of color is $a^*:0.2{\sim}0.8$ and $b^*:-1.1{\sim}2.4$. As a result, the black-colored zirconia was suitable for a artificial jewelry or decoration zirconia goods.

참고문헌 (Reference)

1 X. Y. Wang, "Synthesis of Strong-magnetic Nanosized Black Pigment ZnxFe3-xO4" 74 (74): 269-272, 2007

2 J. S. Lee, "Synthesis of Spinel Pigment on ZnO-Fe2O3 System" 26 (26): 188-1989,

3 A. Escardino, "Synthesis Mechanism of an Iron-Chromium Ceramic Pigment" 83 (83): 29-32, 2000

4 Y. H. Baik, "Study on Synthesis of MgAlO4 Spinel and Characteristics" 22 (22): 29-30, 1985

5 A. Ohtsuka, "Studies on the Pigments of Titanium-Tin and Aluminium-Chrome Spinel" 70 (70): 96-99, 1962

6 A. Ohtsuka, "Studies on Titanium Spinel Pigments" 67 (67): 139-141, 1959

7 A. Ohtsuka, "Research on Tin-Chrome Spinel Pigments Containing Co 2+ and Ni 2+ Ion" 80 (80): 285-299, 1972

8 E. Ozel, "Production and Characterisation of Iron-chromium Pigments and their Interactions with Transparent Glazes" 23 (23): 2097-2104, 2003

9 Y. Shiraki, "Glaze and Pigment" Deakwang 684-, 1980

10 C. W. Park, "Formation and Color of the Spinel Solid-Solution in ZnO-Fe2O3-TiO3-SnO2 System" 31 (31): 213-219, 1994

11 J. S. Lee, "Formation and Color of the Spinel Solid Solution in NiO-ZnO-Fe2O3-TiO2-SnO2 System" 28 (28): 305-314, 1991

12 J. S. Lee, "Formation and Color of the Spinel Solid Solution in CoO-ZnO-Fe2O3-TiO2-SnO2 System" 28 (28): 897-907, 1991

13 A. Ohtsuka, "Formation and Color of the Spinel Solid Solution in CoO-ZnO-Al2O3- Cr2O3-SnO2 System" 84 (84): 76-89, 1976

14 R. A. Eppler, "Cobalt-Free Black Pigment" 60 : 562-565, 1981

15 E. S. Lee, "A Study on the Formation of Spinel Pigment" 12 (12): 25-32, 1975