<P><B>Abstract</B></P> <P>Nanostructured pyropolymers contain significant amounts of redox-active heteroatoms, have high specific surface areas, and a defective carbon microstructure, indicating good potential for pseudo...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107611391
2016
-
SCOPUS,SCIE
학술저널
507-514(8쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P><B>Abstract</B></P> <P>Nanostructured pyropolymers contain significant amounts of redox-active heteroatoms, have high specific surface areas, and a defective carbon microstructure, indicating good potential for pseudo...
<P><B>Abstract</B></P> <P>Nanostructured pyropolymers contain significant amounts of redox-active heteroatoms, have high specific surface areas, and a defective carbon microstructure, indicating good potential for pseudocapacitive charge storage. In this study, nitrogen-enriched pyropolymer nanoparticles (N-PNs-50) are fabricated from polyaniline nanotubes through rapid pyrolysis at 50 °C min<SUP>−1</SUP>. N-PNs-50 exhibit a nitrogen content of 9.8 wt%, a high specific surface area of 875.8 m<SUP>2</SUP> g<SUP>−1</SUP>, and an amorphous carbon structure with an I<SUB> <I>D</I> </SUB>/I<SUB> <I>G</I> </SUB> intensity ratio of 0.95. These unique characteristics lead to good electrochemical performances, in which reversible capacities of 660 and 255 mAh g<SUP>−1</SUP> are achieved for Li-ion and Na-ion storage, respectively, with favorable voltage characteristics (<1.5 V for Li-ions and <1.2 V for Na-ions). This study provides a more feasible production method for nitrogen-doped pyropolymers and their practicable electrochemical performances for use as an anode in energy storage devices.</P> <P><B>Highlights</B></P> <P> <UL> <LI> Nanostructured pyropolymers (N-PNs-50) were fabricated by rapid pyrolysis. </LI> <LI> N-PNs-50 exhibited a nitrogen content of 9.8 wt% and amorphous carbon structure. </LI> <LI> N-PNs-50 exhibited a high specific surface area of 875.8 m<SUP>2</SUP> g<SUP>−1</SUP>. </LI> <LI> 660 and 255 mAh g<SUP>−1</SUP> were achieved for Li-ion and Na-ion storage, respectively. </LI> </UL> </P> <P><B>Graphical abstract</B></P> <P>Nitrogen-enriched pyropolymer nanoparticles (N-PNs-50) were fabricated from polyaniline nanotubes through rapid pyrolysis at 50 °C min<SUP>−1</SUP>, showing superior electrochemical performances.</P> <P>[DISPLAY OMISSION]</P>
Highly efficient and stable cupronickel nanomesh electrode for flexible organic photovoltaic devices