Star-shaped 형태를 기본 골격으로 하는 triazin 화합물을 사용하여 Organic Light-Emitting Diodes(OLEDs) 의 red host material을 합성하였다. 2,4,6-tris(3-methyl-4-(thiophen-2-yl)phenyl)-1,3,5-triazine과 2,4,6-Tris-(3-methyl-4-tr...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=T11205547
춘천 : 강원대학교 일반대학원, 2008
학위논문(석사) -- 강원대학교 일반대학원 일반대학원 , 화학과 , 2008. 2
2008
한국어
강원특별자치도
Efficient Red Host in Phosphorescence Organic Light-Emitting Diodes(PHOLEDs)
55 p.p. 26cm
지도교수:김진호, 강영진
참고문헌 : p.
0
상세조회0
다운로드국문 초록 (Abstract)
Star-shaped 형태를 기본 골격으로 하는 triazin 화합물을 사용하여 Organic Light-Emitting Diodes(OLEDs) 의 red host material을 합성하였다. 2,4,6-tris(3-methyl-4-(thiophen-2-yl)phenyl)-1,3,5-triazine과 2,4,6-Tris-(3-methyl-4-tr...
Star-shaped 형태를 기본 골격으로 하는 triazin 화합물을 사용하여 Organic Light-Emitting Diodes(OLEDs) 의 red host material을 합성하였다.
2,4,6-tris(3-methyl-4-(thiophen-2-yl)phenyl)-1,3,5-triazine과 2,4,6-Tris-(3-methyl-4-trimethy lsilanyl-phenyl)-[1,3,5]triazine을 합성하였다. 이 화합물들은 1H-NMR과 13C-NMR, mass로 구조를 확인하였으며 UV/Vis, Photoluminescence을 이용하여 광 물리적 성질을 조사하였고, TGA, DSC를 이용하여 열적 성질을 조사하였다. UV에서 TMTPT 화합물은 용액상태에서 345nm에서 최대 흡수 피크를 나타내었고 PL에서 393nm에서 최대 발광 피크를 나타내었다. 또한 열적 성질을 조사하였을 때 화합물의 녹는점은 280℃로 높은 열 안정성을 나타내었다. TMSPT는 UV에서 286nm에서 최대흡수파장()을 나타내었고 PL에서 최대발광파장()은 354 nm로 자외선 영역에서 나타났다. 또한 열적 성질을 조사하였을 때 화합물의 녹는점은 321℃로 높은 열 안정성을 나타내었다.
다국어 초록 (Multilingual Abstract)
Star-shaped compounds based on triazine core unit, 2,4,6-tris(3-methyl-4-(thiophen-2-yl)phenyl)-1,3,5-triazine(TMTPT) and 2,4,6-Tris-(3-methyl-4-trimethylsilanyl -phenyl)- [1,3,5] triazine(TMSPT) were synthesized and investigated their application as ...
Star-shaped compounds based on triazine core unit, 2,4,6-tris(3-methyl-4-(thiophen-2-yl)phenyl)-1,3,5-triazine(TMTPT) and 2,4,6-Tris-(3-methyl-4-trimethylsilanyl -phenyl)- [1,3,5] triazine(TMSPT) were synthesized and investigated their application as red host in Phosphorescence Organic Light-Emitting Diodes(PHOLEDs). The structures of all compounds were confirmed by the various spectroscopic methods such as 1H-NMR, 13C-NMR, mass spectroscopy. Thermal stability and photophysical property for TMSPT and TMTPT were also investigated by TGA, UV-visible, photoluminescence. TMSPT is emission with max 354nm and TMTPT is emission with max 383nm was observed. TMTPT shows high thermal stability with the loss of 2% weight at 289 oC. The electroluminescence(EL) characteristics were also investigated. A multilayer EL device with the configuration of ITO/CuPC(10nm)/NPD(40nm)
/TMTPT-[tris(3-Phenylisoquinoline)][tris(3-Phenyl-isoquinoline)]Ir(Ⅲ)(20nm)/Alq3(40nm)/LiF(1nm)/Al(100nm) has been successfully fabricated. External quantum efficiency of 13.3% at 1mA/cm2 was achieved with this new host.