To understand the effect of Y<SUB>2</SUB>BaCuO<SUB>5</SUB> (Y211)/YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-y</SUB> (Y123) interfaces on the oxygen diffusion in single grain YBa<SUB>2</SU...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107748334
Jun, B.H. ; Jung, S.A. ; Park, S.D. ; Park, B.J. ; Han, Y.H. ; Kim, C.J.
2011
-
SCOPUS,SCIE
학술저널
876-879(4쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
To understand the effect of Y<SUB>2</SUB>BaCuO<SUB>5</SUB> (Y211)/YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-y</SUB> (Y123) interfaces on the oxygen diffusion in single grain YBa<SUB>2</SU...
To understand the effect of Y<SUB>2</SUB>BaCuO<SUB>5</SUB> (Y211)/YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-y</SUB> (Y123) interfaces on the oxygen diffusion in single grain YBa<SUB>2</SUB>Cu<SUB>3</SUB>O<SUB>7-y</SUB> superconductors, single grain Y123 superconductors with 0.05 and 0.3moles of Y<SUB>2</SUB>O<SUB>3</SUB> additions were fabricated by a top-seeded melt growth (TSMG) process. Y123 compacts with Y<SUB>2</SUB>O<SUB>3</SUB> additions were subjected to melt growth heating cycles with a cooling rate of 1<SUP>o</SUP>C/h through a peritectic temperature (1015<SUP>o</SUP>C) and then annealed at 450<SUP>o</SUP>C for 200h in flowing oxygen. The superconducting temperature (T<SUB>c</SUB>) and critical current density (J<SUB>c</SUB>) were estimated for the three different regions (top surface (s), intermediate (i) and center (c)) of samples. The amount of Y211/Y123 interface area in single grain Y123 superconductors was successfully controlled by Y<SUB>2</SUB>O<SUB>3</SUB> additions. The T<SUB>c</SUB> values of s regions were higher than those of i and c regions, which indicates the presence of more oxygen at the sample surfaces. In addition, the T<SUB>c</SUB> values of i and c regions of the Y123 sample with 0.3mole Y<SUB>2</SUB>O<SUB>3</SUB> addition were higher than those of the same regions of the Y123 sample with 0.05mole Y<SUB>2</SUB>O<SUB>3</SUB> addition due to the promoted oxygen diffusion through Y211/Y123 interfaces and other related defects. In spite of the promoted oxygen diffusion by Y<SUB>2</SUB>O<SUB>3</SUB> addition, the large T<SUB>c</SUB> difference among the regions still existed, which suggests sluggish oxygen diffusion into single Y123 grains.
Characterization of reactors for integrated matrix-type SFCL