Wear of Retrieved UHMWPE Hip Liners
이권용,김신윤,신대환,이성재,김석영 연세대학교의과대학 2004 Yonsei medical journal Vol.45 No.2
After the gamma-irradiation sterilization, the most widely used orthopaedic grade polymer bearing liner material for the total joint replacement, ultra-high molecular weight polyethylene (UHMWPE), degrades through the progressive in vivo oxidation. The oxidative degradation makes UHMWPE brittle and leads to reduction of its mechanical properties. In this study, the effect of the in vivo post-irradiation ageing time on the wear of UHMWPE was investigated. Twelve retrieved polyethylene hip liners implanted for 3-16 years and then stored in the air for 1.5-8 years were used. Two types of the pin-on-disk wear testing were conducted. The uni-directional repeat pass rotating and the linear reciprocating wear testing were done with stainless steel disks against stationary polyethylene pins under 4MPa at 1Hz with bovine serum lubrication. Wear of the retrieved polyethylene hip liners does not have significant correlation with the in vivo or total ageing time. The linear reciprocal sliding motion generated a more pronounced wear than the uni-directional repeat pass sliding motion. This indicates that the kinematic motion significantly affects the wear of aged UHMWPE, having a brittle, white band region.
두가지 기구운동을 하는 타이타늄 합금과 스테인레스 스틸 디스크에 대한 초고분자량 폴리에틸렌 핀의 마멸
이권용,김석영,김신윤 한국트라이볼로지학회 2002 한국윤활학회지(윤활학회지) Vol.34 No.1
The wear behaviors of ultrahigh molecular weight polyethylene pins against titanium alloy and stainless steel disks moving in two different kinematic motion were investigated by conducting repeat pass rotational sliding and linear reciprocal sliding wear tests. Linear reciprocal motion wore more the polyethylene pin than did repeat pass rotational motion for both disk materials. It means that the repeated directional change of contact stresses generates more wear debris in polyethylene. For the linear reciprocal sliding tests, titanium alloy disks were damaged with some scratches after one million cycles but no surface damage was observed on the polyethylene pins. On the other hand, fur the repeat pass rotational sliding tests, all titanium alloy disks were severely abraded on the entire region of sliding track. This phenomenon can be interpreted by that stress fatigue under repeated sliding contact initiated titanium oxide layer wear particles from disk surface, and these hard particles were embedded into polyethylene pin and then they severely abraded the disk surface. From these results it can be concluded that the kinematic motion in pin-on-disk wear tests play a crucial role on the wear behaviors of UHMWPE pins against titanium alloy and stainless steef discs.