SHS 공정에 의한 열전대 보호관용 $ZrB_2$ 세라믹스의 제조
곽철상,김상배,이윤복,박홍채,오기동 한국세라믹학회 1997 한국세라믹학회지 Vol.34 No.11
ZrB2 powders were prepared from a mixture of ZrO2, B2O3 and Mg by self-propagating high temperature synthesis method. The combustion product was successfully obtained from a mixture of ZrO2:B2O3:Mg=1:2:8.5 molar ratio. By-product, MgO was effectively removed by leaching with 1M HCl solution at 9$0^{\circ}C$ for over 5hours. After leaching, the Mg content was 0.86~1.42 wt%, and the mean particle size was 4.72${\mu}{\textrm}{m}$. The addition of 7.5 wt%(14Ni:1.0C) as a sintering aid greatly densified ZrB2 bodies compared with that of only Ni. The ZrB2 sintered bodies containing 7.5 wt%(14Ni:1.0C) was 94.3% of the theoretical density. In this case, ZrB2 existed as a major phase and had a bend strength of 300 MPa and a vickers hardness of 2000 kg/$\textrm{mm}^2$.
SHS법에 의한 붕화지르코늄의 합성 및 치밀화에 미치는 첨가제의 영향
이윤복,곽철상,김상배,김영우,박홍채,오기동,Lee, Yun-Bok,Gwak, Cheol-Sang,Kim, Sang-Bae,Kim, Yeong-U,Park, Hong-Chae,O, Gi-Dong 한국재료학회 1998 한국재료학회지 Vol.8 No.7
ZrO2, B2O3 및 AI을 사용하여 SHS법에 의한 붕화지르코늄을 합성을 하고 산화철과 알루미늄 분말의 첨가가 합성물의 치밀화에 미치는 영향에 대하여 검토하였다. 합성물중에 존재하는 결정상은 대부분이 ZrB2와 $\alpha$-AI2O3상이었다. 산화붕소와 알루미늄의 몰비가 1.0:3.3이상일 때 합성물의 치밀화는 크게 증가하였고, ZrB2 입자도$\alpha$-AI2O3용융상과 더불어 조대하였다. 산화철 1목에 대하여 알루미늄을 1-3몰을 첨가한 것과 산화철 1.5몰에 대하여 알루미늄을 3몰 첨가시 $\alpha$-AI2O3를 중심으로하는 슬라그상으로부터 용융상의 분이가 가능하였고, 이들 용융상에 존재하는 결정상은 ZrB2이외에 Fe, Fe2B, Zr2Fe상이었다. 용융상의 상대밀도는 산화철 1몰에 대하여 알루미늄을 1몰 첨가시 83.2%인 반면에 그 이상의 첨가량에 대해서는 치밀화는 크게 증가하여 알루미늄을 3몰 첨가한 경우 상대밀도는 93.7%로서 최대를 나타내었다.